Electronics Forum | Fri Nov 08 11:37:44 EST 2002 | jonfox
1. Back in the early days of consumer digital cell phones, we ran into the same problem. PCB with 2000 parts in a 5"x2" area, and double sided. We ended up using our standard vacuum tooling for the NIC side and stiff ESD safe foam for the NAC side
Electronics Forum | Mon Jul 19 09:53:07 EDT 2004 | Mighty C
Good Morning Rush Fan, We have a Metcal VPI 1000. We are very happy with the system. The price is competitive, software is easy to use and the picture quality is good. They have a great lighting scheme that illuminates under a BGA extremely well. Th
Electronics Forum | Wed May 16 11:40:11 EDT 2007 | stepheniii
I test pdb-boards on the mat it ain't work! Wrong > mount of bolts being outputted. is have something > to do witfh the rohas soulder on them? I will take a stab at translating. I test PCBs on a static mat but the test does not work. The output
Electronics Forum | Wed Nov 21 09:19:09 EST 2007 | Paul M.
Need some opinions from you fine folks. We are building assemblies 90% SMT, 10% TH. Fine pitch and BGA devices, etc. The customer is complaining about cold solder joints (SMT) after about 1 year of use, scattered thru-out the assembly, not consistan
Electronics Forum | Fri Apr 26 05:50:54 EDT 2019 | ppcbs
We just apply tacky flux to the surrounding components and to the bottom side components under the BGA. This will prevent cold solder if any solder joints reach reflow temperature the surface tension will keep them aligned and in place. If you nee
Electronics Forum | Wed Apr 21 20:50:26 EDT 1999 | Dave F
| I'm having problems with trying to get a good solder joint using a Ceramic PCB. We are using AMTECH hi-temp solder (ws-486 96.5/3.5ag). My profile looks great and I used the recommended profile from Amtech with a few adjustments. My max temp is abo
Electronics Forum | Thu Apr 16 23:59:45 EDT 1998 | Mike C
| Hello Ya'll, | I've got what may be a silly question, but why does it seem so important to everybody that you have x-ray capability if you're thinking about doing BGA? | I know what most people will tell me; "Steve, that's a pretty silly qu
Electronics Forum | Thu Dec 14 12:18:01 EST 2000 | genny
Hello all, Our company has always used HASL finish on our products. Recently however, we have a had a problem on a couple of boards that I have been told cannot be avoided with HASL, and we should switch to ENIG(electroless nickel immersion gold).
Electronics Forum | Fri May 29 08:25:13 EDT 2009 | floydf
We are getting what looks like cold solder joints on one of our boards. The boards have an aluminum substrate, and use OSP plating. The solder is lead free - 96.5 Sn, 3.0 Ag, .5 Cu. The flux is no clean. When we first had the problem, my solder profi
Electronics Forum | Tue Aug 24 15:05:39 EDT 2004 | Dreamsniper
There is danger in doing this based on theory. Chances of the solder joints becoming cold or having poor wetting due to the fact that during the first run all the flux vehicles had evaporated and with the second run they're no longer present to help