Electronics Forum | Mon Aug 28 17:04:52 EDT 2006 | Board House
ImSn - Immersion Tin - Not Recomended- short shelf life ImAg - Immersion Silver - Prefered Surface finsh by most Board houses, Best reworkablility, 12 moth self life, ENIG - Electroless Nickel Immersion Gold - Second Choice for Board Shops, 12 -
Electronics Forum | Thu Jul 10 09:55:47 EDT 2003 | davef
A reading of the pictures is: A1: Looks like pad [B1] is smaller than the other pads. It�s weird that the pads are such different colors. A2: Looks like pad [B1] is smaller than the other pads. Solder mask opening [B1] is misregistered and seems s
Electronics Forum | Fri Jul 09 18:36:48 EDT 2010 | rway
We don't use flex pcbs but have the same issue here. Most of our pcbs are HASL finish. I have looked at silver and gold immersion and both look really good under my color camera on my AOI. However, gold is more pricey. There is no additional cost
Electronics Forum | Thu Dec 14 12:18:01 EST 2000 | genny
Hello all, Our company has always used HASL finish on our products. Recently however, we have a had a problem on a couple of boards that I have been told cannot be avoided with HASL, and we should switch to ENIG(electroless nickel immersion gold).
Electronics Forum | Fri Nov 16 08:10:56 EST 2001 | Matt Kehoe
Hi Dave. Sorry I have not responded. Just as I was getting into this forum activity the company I worked for (past tense) decided not to re join the SMTA and I was cut off. Anyways, you can find most of what you asked for about SIPAD on the Midwest
Electronics Forum | Sun Aug 08 11:15:32 EDT 1999 | Earl Moon
| | Mike, | | | | Got your message and those of others concerning PCB fab supplier evaluation and qualification check lists, etc. I have a severe problem here in WI as I can hardly access the internet, and when I do it is cut off abruptly for no goo