Hi, Wow, that's cheap. I did not know they were available that low cost, and we had been quoted much higher for the Ursa scope, so that's why I thought why bother, and lets put it into xray. I bet Superman would have a terrible time working in an S
Electronics Forum | Wed Mar 14 17:11:57 EST 2001 | davef
First, x-ray inspection machines have a wide range of capilities. Resolution is a key measure of a machine's ability to "distinguish" features. People say that some x-ray inspection machines have the ability to position the board being inspected at
Electronics Forum | Thu May 30 10:31:03 EDT 2002 | robbied
Hi Yannick. This is an issue that we are just recently getting into but here is some ifo that I have gathered so far. I have seen/ used 2 different rework machines. The one we have bought is a 'PACE TF2000' which was at the lower cost end of the mar
Electronics Forum | Tue Apr 03 01:37:54 EDT 2001 | philipreyes
60% 36% 0f ball area >36% Class2 Accept Reject 45% of ball diameter >45% 20.25% of ball area >20.25% Class3 Accept
Electronics Forum | Wed Mar 14 16:30:02 EST 2001 | CAL
Reading x-rays is an art. All balls should be symmetrical in size and shape. Please provide more information on your question. Why just opens? If the Balls are not consistently the same in size or shape there is a problem. Larger balls could be from
Electronics Forum | Wed Dec 14 06:58:29 EST 2005 | jdumont
We have a version of the SMT Tools scope. We use it hand held style with no stand (much easier). We also find that it is not used very often. XRay and a reliable process are more important to spend the time and money on. This is a good tool to have f
Electronics Forum | Fri Dec 02 18:37:46 EST 2005 | Ola
What is the quality worth to You? How much is "to much" for You to spend on a good quality ckeck? How much benefit can You get in return, If You in the first place get the processes straight? These are the main questions that You have to answer Yours
Electronics Forum | Thu Apr 27 21:20:38 EDT 2000 | Dean
Here are some pointers to use during your X-ray inspection. Microcracking is virtually impossible to determine with X-ray. However, I suspect you are looking for "hard" opens. Those are much easier to find visually. If using a paste-and-place pro
Electronics Forum | Tue Oct 11 03:50:24 EDT 2022 | ky
Hi Everyone, we have here in our EMS supplier some finish goods that pass all our functional test but fail our final burning test. The burning test is a 30 minutes test which simulate customer use cases, during this test the product is subject to tem
Electronics Forum | Thu Apr 27 21:04:33 EDT 2000 | Dave F
Ron: Good news: Nicolet makes excellent machines. Bad news: I�m unaware of a machine with the capabilities you seek. * X-ray machines lack of resolution needed in relation to the crack geometries encountered within a high density single material.
Our Company handle AOI (Auto Optical Inspection) and SPI (Solder Paste Inspection) Machines.
Equipment Dealer / Broker / Auctions
Hwaseong-si, Gyeonggi-do, Korea
Hwaseong-si, South Korea
Phone: +82-1029254936