Electronics Forum | Wed Mar 30 14:51:19 EST 2005 | Cmiller
We are looking at switching to UV cure for faster throughput. Does anyone know of any cost effective coating manufacturers? The pricing we are getting back are around $250.00 a gallon in 5 gal pails. This is more than twice what we pay for our curren
Electronics Forum | Tue Feb 03 15:14:58 EST 2015 | stevezeva
This is a late reply, but from my experience a really good removal station is one made by a company called CCRCo. They make a micro-abrasive station that addresses all the ESD concerns. They utilize a reusable media that is really cost effective. The
Electronics Forum | Fri Sep 11 12:08:10 EDT 2015 | derrikf
I built one using an old Asymtek Automove. When all was said and done, it cost less than $400, including what was paid for the machine itself. It's a very basic setup, (air over syringe), but for our needs it does everything and more. With air to syr
Electronics Forum | Tue Dec 01 09:24:01 EST 2009 | sforman1
40 years. no cost to you. just trying to help Sam
Electronics Forum | Wed Nov 09 12:23:34 EST 2005 | SuMoTe
Caplugs Very low tech, and very low cost. you will have to do a bit of work to find a size that will work for you, but the savings are worth it.
Electronics Forum | Fri May 15 19:08:25 EDT 2009 | jlawson
Ammonia based masks can create solderability issues after they are removed. You can get non-ammonia based latex mask material but down side is slower cure and cost a little more as they have higher levels of latex etc
Electronics Forum | Fri Apr 21 17:46:29 EDT 2006 | SD
First of all, do not use kapton tape! It tends to cause a dewetting effect around the tape. A call to Humiseal will explain why. There's not really a blanket answer to your question.... Removing cured liquid mask can often result in a fillet ef
Electronics Forum | Wed Jun 03 07:13:27 EDT 1998 | Tom Tellinghuisen
| We have experienced poor adhesion of acrylic conformal coating to plastic bodied IC�s. The observed symptoms of this are a blistering or lifting of the coating at the surface of the component, although peel testing has revealed that this is not al
Electronics Forum | Wed Jun 03 15:22:12 EDT 1998 | Greg Curler
| | We have experienced poor adhesion of acrylic conformal coating to plastic bodied IC�s. The observed symptoms of this are a blistering or lifting of the coating at the surface of the component, although peel testing has revealed that this is not
Electronics Forum | Tue Jun 16 11:29:16 EDT 2009 | operator
Does anyone have ballpark figures readily available for how much conformal coating machines cost? Benchtop and In-line? New and Used? I am really curious and considering purchasing, but don't want to go stir up a hornets net of salesman at this po