Electronics Forum | Tue Nov 08 05:00:23 EST 2005 | rlackey
Hi CW, Regarding orientation, yes, your diagram is right - see the following link for confirmation. http://search.murata.co.jp/Ceramy/image/img/A18X/C2EB3C.PDF Regarding information on bending strength you want to talk to your local Murata office
Electronics Forum | Thu Oct 02 11:04:48 EDT 2003 | russ
Out of curiousity, Isn't soldermask only used as a solder processing aid and to cover the copper? Russ
Electronics Forum | Mon Oct 06 12:37:18 EDT 2003 | ramanandkini
It was a nice discussion. What I did here was a thermal shock test 1 hour@ +90 deg.c and immediately 1 hour @ -40 deg.c. The second test I did was a high humudity test for a week. After each test, I carried out a peel test with scotch tape. Those bo
Electronics Forum | Mon Feb 19 17:34:02 EST 2007 | GS
Thank You Pavel and Dave, Unfortunately I do not have IPC-4554. Anyway I 0.6-1.0umm is what I remember, and confirmed by reading also through leterature available on google. I was just going to understand if it possible to obtain more thickness
Electronics Forum | Tue Apr 24 09:19:51 EDT 2018 | vetteboy86
Is there a preferred method among printed circuit board assembly for accurately and quickly verifying the copper weight of a printed circuit board? I would like a tool and process that our quality inspector could quickly use to verify upon receipt of
Electronics Forum | Sat Sep 04 18:52:51 EDT 2004 | iqbalb
Yes it is vital for process control.
Electronics Forum | Sat Sep 04 11:58:44 EDT 2004 | Dhanashekar
Can anyone suggest me if it is necessary to measure the paste thickness after contact Screen printing.Is it a very vital parameter for the production process?
Electronics Forum | Fri Apr 16 11:03:35 EDT 2004 | davef
Your copper corrosion is not good. It indicates that you have not done a good job in cleaning. [We assume this is a medium green color, not unlike the color of the solder mask on your board, that is almost like a translucent lacquer; rather than th
Electronics Forum | Thu Sep 09 04:15:36 EDT 2004 | Rob
Hi Chris, We use MPM's, where you can set the paste inspection to look at whatever you want it to (remember this does slow cycle time down) and we swear by them. However I have also met many happy DEK users who believe their machines are equally as
Electronics Forum | Mon Dec 20 07:58:02 EST 1999 | pascal MATHIEU
hello guys ; we are using a fine pitch component(0.65mm) on a thick copper PCB (Cu = 90�m) ; in this case we notice that we are in the process'limits , because the different supplier of the PCB are not able to ensure a good stability of it's process