Electronics Forum | Fri Jun 27 22:33:16 EDT 2003 | Ben
HI, I'm doing a dye penetrant and peel test of non-function BGA solder joints to locate the fracture surface. After applying dye, I found the dye ink just accumulate at the solder mask edge and spread everywhere after I peeled off the package. THis i
Electronics Forum | Sat Jun 28 08:17:21 EDT 2003 | davef
We form a barrier to contain the dye, but regardless it is messy. Actually, we no longer use dye, per say. We use the stuff machinists use for staining metal. Look here for hints: * http://www.ivf.se/Elektronik/dye_penetrant/edefault.htm * http:
Electronics Forum | Thu May 26 08:52:42 EDT 2011 | davef
Phil Zarrow wrote a useful paper that could help in evaluating paste. Here read it ... Evaluating Solder Paste � Not An Option Contributed by Phil Zarrow of ITM an Independent SMT consulting firm With soldering being the dominant source of assembly
Electronics Forum | Wed Mar 04 13:06:45 EST 2015 | cyber_wolf
A full blown analysis could become very expensive. There are many test that can be performed. 3D acoustic microscopy, X-ray, Dye and pry,and I'm sure the list goes on. Typically, a micro-cross section report of the BGA solder joints will show you w
Electronics Forum | Sat Oct 09 03:45:34 EDT 1999 | Brian
| Right now,we have some problem on SMT. Cause of the flux residue | in the connector. Do somebody have the same symptom? By the way, | can i find something to make the flux observe easy or take a photo with the flux. | | | Unfortunately, this pr
Electronics Forum | Wed Apr 23 21:34:24 EDT 2008 | fowlerchang
It is CSP reliability issue, which is the mobile CPU from Spreadtrum. All the tests passed and shipped to customer. They assembly them and tested but failed. After they reflow this CSP with hot air gun, some of the boards passed. We got some board
Electronics Forum | Fri Oct 14 09:21:36 EDT 2005 | lupo
According with temperature vs. wetting force diagram 245-250C/degrees is better, so lower temperature than 500F means better solder fill. If the speed is too lower the solder suck out form the hole. Usually 120-150cm/min. is good. (2-4s contact
Electronics Forum | Fri May 07 15:58:36 EDT 2010 | smt_guy
I'm looking for an optical scope that can penetrate through a gap of 0.005" to 0.010". Is there anything available in the Electronics / Semiconductor Industry for this kind of application? I want to see what's inside that size of gap for solder short
Electronics Forum | Tue Apr 22 03:46:19 EDT 2008 | fowlerchang
It is CSP reliability issue, which is the mobile CPU from Spreadtrum. All the tests passed and shipped to customer. They assembly them and tested but failed. After they reflow this CSP with hot air gun, some of the boards passed. We got some board
Electronics Forum | Wed Sep 12 18:11:03 EDT 2001 | davef
First, what on the area array package are you analyzing � * Package cracking? * Cracked solder balls? * Er, what? Second, most failure analysis discussions consider dye penetration to be a non-destructive test, but then again most failure analysis