Electronics Forum | Thu Feb 02 10:10:20 EST 2023 | tommy_magyar
Perhaps google this, as you will find very interesting articles. For scientific explanation look up solder fatigue on Wikipedia with references added. A more in depth explanation you can find on the Digikey forum where you will find other people like
Electronics Forum | Tue Apr 08 15:27:33 EDT 2008 | arminski
hi experts, need more info on what's happening with the LPI Solder Mask on an FR4 PCB during reflow of both Leaded and Lead Free Process? Do they become soft as well while exposed to the extreme temperatures? regards,
Electronics Forum | Fri Aug 20 13:36:46 EDT 2004 | ttye01
We conduct temperature stress test (-40 to +100C)on our products which sits on our expensive test board. This stress test on our product shorten the life span of the test board due to the extreme temperature change. I have tried epoxy coating on the
Electronics Forum | Thu Feb 11 12:02:47 EST 2010 | plaiming
We have temporarily switched to an RTV for the vibration reincforcement, but it is not compatible with acrylic conformal coating and we really do not want to switch conformal coatings to a silicone based. Additionally we are testing the product in h
Electronics Forum | Wed Feb 11 14:55:52 EST 2015 | erezah
we received assembled PCBs with spots that look like a bleach spots all over the PS and CS . The board house said that this is normal due to flux aqueous wash process. Can it cause problems (e.g. corrosion ) in the long run or cause issues when wor
Electronics Forum | Thu Sep 13 11:01:39 EDT 2007 | cyber_wolf
Fuji specs out Omega 66 grease for the solenoid sliders on older CP machines. These solenoids run hot. Its interesting to me that this grease is designed for extremely low temperature applications. Whats up with that ? http://www.omegaoil.co.jp/ind
Electronics Forum | Mon Oct 18 20:06:27 EDT 1999 | Phuc Nguyen
I am researching a process call Collumn Grid Array for the BGA. Please email me if you have some knowledge about this process. The problem is ceramic BGA has different thermal coefficient with PCB (FR-4) material, and in extreme temperature (-40 C-
Electronics Forum | Tue Nov 27 16:58:29 EST 2001 | davef
We wave solder no MELF. When we analyzed this a couple of years ago, the temperature extremes of the wave affected LT reliability.
Electronics Forum | Tue Aug 23 14:23:00 EDT 2005 | pjc
Most ovens I know use oil to lubricate conveyor chain, not grease. Anyway, is this what you're using: NMG No Melt Grease NLGI 2 (operates from -20�C to +270�C) NMG is a long-fibred highly adhesive grease which does not melt or drip at high temperat
Electronics Forum | Tue Aug 22 11:17:04 EDT 2000 | Dr. Ning-Cheng Lee
The classic dilemma, cost vs. performance. In typical applications, Sn whisker growth is not an issue. It only seems to occur under extreme use (high stress, low temperature)conditions. Until this issue is fully addressed, Pd seems to be the favor