Electronics Forum | Wed Aug 25 14:40:24 EDT 1999 | hammer
Has anyone used bar solder from a company called "Electrum Inc." What kind of results did you have?
Electronics Forum | Thu Aug 26 08:15:13 EDT 1999 | Brian
| | Has anyone used bar solder from a company called "Electrum Inc." | | What kind of results did you have? | | | | | Hammer: Try: | | Electrum Recovery Works 827 Martin St Rahway, NJ 07065 908-396-1616 800-622-1192 Canada 800-535-1192 Fax: 908-3
Electronics Forum | Wed Aug 25 19:46:25 EDT 1999 | Dave F
| Has anyone used bar solder from a company called "Electrum Inc." | What kind of results did you have? | | Hammer: Try: Electrum Recovery Works 827 Martin St Rahway, NJ 07065 908-396-1616 800-622-1192 Canada 800-535-1192 Fax: 908-396-9390 John S
Electronics Forum | Thu Aug 26 08:17:07 EDT 1999 | Brian
| | Has anyone used bar solder from a company called "Electrum Inc." | | What kind of results did you have? | | | | | Hammer: Try: | | Electrum Recovery Works 827 Martin St Rahway, NJ 07065 908-396-1616 800-622-1192 Canada 800-535-1192 Fax: 908-3
Electronics Forum | Wed Aug 23 14:59:32 EDT 2006 | bill
I�ve been lurking on the forum for a while so I will take a stab at this, mainly because there is no answer I take it that you have a variety of boards being produced at the same time and are in fixtures so the conveyors don�t need to be adjusted, a
Electronics Forum | Wed Jan 07 12:09:40 EST 2004 | Kris
Hi All, Does any body have any information on hot bar lead free soldering ? Need papers or experimental data ASAP Thanks
Electronics Forum | Thu Jul 31 13:42:08 EDT 2008 | comatose
I'm looking to fill a solder fountain with 50lb of SN100C. My usual source for paste and the like doesn't stock this alloy. We run double sided reflow, so we're not going to be needing hundreds of pounds for a wave machine at any point. Who is the
Electronics Forum | Fri May 12 13:56:37 EDT 2006 | timnop
Steve, Thank you very much for your reply. What I really need to know now is how you discovered these issues. Did you run this product in your wave solder machine, and for how long? Are you now using SN100c instead? Please mention the other issues if
Electronics Forum | Mon May 15 11:26:41 EDT 2006 | russ
Tim, call kester and ask for references who better than them to tell you who is using. Russ
Electronics Forum | Fri May 12 12:07:10 EDT 2006 | solderiron
The kester better known as KY'd Sn/Cu has more copper intermetallic growth over time, dissolves copper from the board faster so repairing and touchup can damage board. Bridges more than SN100c. Does not thermal cycle well. Has shrink cracks that can