Electronics Forum | Tue May 08 10:31:04 EDT 2007 | Yankee
Hi all, I think Hot Tear or Shrink Hole defect is common in LEAD FREE wave soldering, especially those solder is from SAC type. As far as I know, it is related to cooling rate. Is there anyone know how to solve or reduce this defect at wave solder
Electronics Forum | Wed May 09 11:01:27 EDT 2007 | callckq
Yes, continue to use SAC solder. However, as far as I know, the problem become more severe when cooling rate is increased.
Electronics Forum | Tue May 08 22:34:53 EDT 2007 | davef
Do you mean "how to solve or reduce this defect at wave soldering process" while continuing to use-up my SACX solder? If so, try: * Smaller solder volumes lower shrinkage hole / hot tears [Higher hole diameter versus pin diameter helps in reducing v
Electronics Forum | Tue Aug 02 22:49:55 EDT 2005 | davef
IPC-A-610D Section 5, shows a variety of photographs of: * Good lead-free solder connections * Lead-free soldering anomalies Hot Tear / Shrink Hole is one such anomaly. This shrinkage effect appears primarily on wave-soldered joints, but can also
Electronics Forum | Thu Jul 13 22:20:38 EDT 2000 | Dave F
=10 mils larger than lead 3 silk screen legend text weight >=10 mils 4 pads >=15 mils larger than finished hole sizes 5 place through hole components on 50 mil grid 6 no silk screen legend text over vias (if vias not solder masked) or holes 7 so
Electronics Forum | Tue Aug 05 01:13:22 EDT 2008 | Sean
Dear all, As far as I know hot tear or shrink hole defect only happen at plated though hole soldering, especially for those lead free wave process. Recently, a laboratory engineer had done cross section on some of the SMT BGA ball and IC lead solde
Electronics Forum | Thu Mar 23 22:26:53 EST 2006 | Joseph
Dear all, Referring comment from Mr. Jack,IPC director certification & assembly technology, the term "fillet tearing" is too broad. Cracks or fractures in the required fillet area, with SnPb or LF alloy and whether you call it tearing or not, is a D
Electronics Forum | Tue Aug 01 09:42:07 EDT 2000 | Gary
The Technical Services Group at Alpha Metals has spent a fair amount of time looking at wave soldered Pb-free connections. We too have observed fillet tearing, fillet lifting, and pad lifting. I have concluded that without major changes in the mate