Electronics Forum | Tue Aug 22 14:59:55 EDT 2000 | Mike Naddra
What does the reflow profile look like , the question I had was surrounding the higher reflow temperature and the max temperature that lowest thermal mass components will see. Some other questions that I had were surrounding the components , what of
Electronics Forum | Thu Jan 15 15:13:50 EST 1998 | justin medernach
| I have a problem! The solder on my pc boards look great comeing out | of my reflow oven. They go thrue the rest of the prossese | and at the end at the qc station it's cold or whitish or gray not shiny. | does any one have a idea on how to correct
Electronics Forum | Wed Apr 16 16:55:38 EDT 2003 | russ
Thanks for the info, Here is a couple more questions (and you thought you were done) What size are these caps /res? how thick is your stencil? what type of oven are you using? what is the finish of the board? Anyway, it seems like (from a distance)t
Electronics Forum | Thu Dec 16 16:46:47 EST 1999 | Mike Naddra
Steve , I use a general set of guidlines when developing reflow profiles: Ramp rate to 140 deg C - 50-60 seconds Time at preheat (140-160 deg C) - 90-120 sec Time above liquidous (183 deg C) - 45-90 sec Time at peak (215-225 deg C) - 9-12 sec peak t
Electronics Forum | Thu May 26 08:52:42 EDT 2011 | davef
Phil Zarrow wrote a useful paper that could help in evaluating paste. Here read it ... Evaluating Solder Paste � Not An Option Contributed by Phil Zarrow of ITM an Independent SMT consulting firm With soldering being the dominant source of assembly
Electronics Forum | Fri Sep 24 10:57:18 EDT 1999 | Earl Moon
| Hi Folks: | | We've been having bridging problems on our fine-pitch QFP's, despite thorough inspection of paste height, volume, and placement accuracies....profiles look good also. | | The bridging is happening after coming out of reflow...one la
Electronics Forum | Wed Oct 03 17:07:52 EDT 2001 | davef
We have had soldering problems with fine pitch QFP in the past [and probably will in the future]. Several questions leap to mind: * When you took your profile on the component pads, do you profile on the pads that did not solder well? * When you say
Electronics Forum | Fri Feb 27 11:33:32 EST 2004 | Bryan
Very strange question,but interesting.Is there anyone who have conducted any experiments to figure out the results?I made a profile board,one thermal couple on pad and other one drilled into the ball of BGA.the 2 points are perpendicular to conveyor
Electronics Forum | Sun Mar 07 08:19:24 EST 1999 | Earl Moon
| | | | | | | | I'm having a fun time between BGA rework/repair using an SRT 1000 and SPC efforts (much easier) using DEK stencil printing processes and BTU reflow with 6 Fuji lines in between. | | | | | | | | Concerning the BGA stuff, I'm getting
Electronics Forum | Thu Aug 10 13:12:10 EDT 2000 | Bob Willis
You may care to review the following from my Circuits Assembly page on line. "HOW FLAT IS FLAT AND DO WE NEED FLAT CIRCUIT BOARD, YES WE DO ? As production problems go there is one that keeps reoccurring time and time again. The blame is usually di