Hi Experts, I need help here, advice appreciated from all... Production is running a Lot of flex-circuit PCB, through the SMT line, with 0402 components. The flex-PCB is taped to FR4 support "pallets" when processing thru' the SMT P&P m/c. We use
Electronics Forum | Thu Oct 23 09:49:18 EDT 2008 | davef
We're not sure the specifics that BLT Circuit Services Ltd referenced, but many companies use dross reducing agents in their wave solder pots. Among dross reducing agent suppliers: * Fry [4100 Sixth Ave, Altoona, PA 16602; 814-946-1611 F814-944-8094
Electronics Forum | Fri May 22 17:48:48 EDT 2015 | aemery
It's your first line, go with established manufacturers. Whether new or used it ultimately comes down to does the tool do the job and how well is it supported (labor/parts) if it does break down. I am a former field eng. with Speedline and now run
Electronics Forum | Thu Aug 30 11:59:00 EDT 2001 | Spanky
Hey all, I have 3 questions about reflow. Hopefully someone can help me. 1. I am having a problem. I set the peak at 230 and my mole thermocouples are telling me the temp in that zone gets to 237. How is this possible even if the thermocouple
Electronics Forum | Wed Sep 05 17:37:56 EDT 2001 | seand
Hello Jeff, If you have components on your board be careful of how low the frequency is that you will be applying to your board. Ultrasonics are great for cleaning stencils and bare boards at around 40kHz. These frequencies (and Lower)may however