Electronics Forum | Thu Jan 29 05:13:35 EST 2015 | neeraj_iiser
how to solder manganin 0.05mm manganin wire to a copper plate
Electronics Forum | Fri Jan 30 00:41:04 EST 2015 | neeraj_iiser
Thanks a lot , my application is cryogenic in nature. I am trying to make a Sub-Angstrom resolution Thermal expansion sensor, whose components have been machined out of OHFC copper, and i needed to solder a manganin wire to one of the capcitor plates
Electronics Forum | Thu Jan 29 09:18:36 EST 2015 | davef
Nichrome, manganin, phosphor bronze etc are easy to solder ... the hard part is removing the corrosion * Manganin: 86% copper, 12% manganese, 2% nickel. Often, it's used in making cryogenic measurements, due to its low heat loss. * Select a flux for
Electronics Forum | Sun Apr 15 23:35:14 EDT 2007 | Sam
few more questions: Is there any standard saying that the dull surface is accepted if solder Au plated leads? Understand that more than 3% Au in the solder connection leads to unacceptable embrittlement of the connection. How about any standard relat
Electronics Forum | Mon Jul 08 22:03:39 EDT 2019 | eddy2019
Many beginners do not know how to start learning hardware circuits. In fact, the "hardware circuit" is composed of a part of the "unit module circuit". The so-called "unit module circuit" includes: various regulated power supply circuits (like the LM
Electronics Forum | Thu Nov 03 04:31:21 EST 2005 | arnold
davef, how can you convince me that 100Sn dissolved copper much faster?
Electronics Forum | Thu Nov 03 08:18:17 EST 2005 | fctassembly
Hello Arnold, Just to clarify the Sn100C discussion: Please note that SN100C is the Nihon Superior alloy composed of tin/.7copper/nickel. The key point in regard to SN100C is that Cu does not go directly into solution but first reacts to form an inte
Electronics Forum | Tue Jun 20 08:30:31 EDT 2006 | dougs
It's hand solder, the wires are free issued, what i'm finding is that if we keep the heat and push enough solder into the joint that the component side wets there is that much solder moved up the wire that it goes solid. this is no good as the custo
Electronics Forum | Wed Dec 07 17:43:31 EST 2011 | mikenil
Hi I do not work for a board house but a manufacturing facility where we do a considerable amount of soldering wires to through holes. We pretin our through holes on both sides of the PCB prior to reflowing the solder and installing the conductor (w
Electronics Forum | Wed Dec 20 15:40:36 EST 2006 | slthomas
I'm no metallurgist but I don't think you're going to burn up lead with a soldering iron. That said, I would surmise that you could pull a lot of the metallization from the component terminations (very likely lead free) and the pads on the board (i