This is not about the physical laws but besides contamination, which will actually IMO cause NO WETTING, it is quite vital that the time-limit the flux is active is not exceeded during your reflow process. Depending on your paste/flux you will have a
Electronics Forum | Thu Nov 01 12:13:10 EST 2001 | jonathan
I guess this clarifies the defect more then looks at the process, but I�ll just through it out there for the sake of learning something new. If anyone would comment on this please feel free�. There are many different varieties of dewetting defects.
Electronics Forum | Fri Apr 21 17:46:29 EDT 2006 | SD
First of all, do not use kapton tape! It tends to cause a dewetting effect around the tape. A call to Humiseal will explain why. There's not really a blanket answer to your question.... Removing cured liquid mask can often result in a fillet ef
Electronics Forum | Wed Nov 01 09:01:55 EST 2000 | Thomas Ballhausen
Since your problem has been posted quite some time ago I am eager to know, if you have got any clue. One of my customers recently claimed our 313-PBGA causing problems, as one of its balls (randomly) is almost dewetting. So no evidence is found by x-
Electronics Forum | Wed Aug 15 16:04:23 EDT 2001 | davef
First, responding to your question � Several things on copper dissolution in solder are: * A 50um copper wire will dissolve in 60Sn / 40Pb solder at: - 200�C solder in 55 seconds; - 250�C solder in 20 seconds; - 300�C solder in 5 seconds; - 350�C so