Electronics Forum | Wed Jul 21 13:18:19 EDT 2004 | patrickbruneel
Thomas, The first thing I would suggest you to do is identify the type of problem your dealing with �pinhole� or �blowhole� before you can take the appropriate action to correct the problem. A pinhole is a void or cavity caused by non-wettable part
Electronics Forum | Thu Jun 20 08:47:51 EDT 2002 | Patrick
I would suggest you try the acrypeel 2000 peelable mask from Interflux USA. Try this link for more info http://www.interfluxusa.com/Datasheets/Acrypeel2000.htm Good Luck
Electronics Forum | Wed Jul 31 10:55:06 EDT 2002 | patrickbruneel
Christopher, Is it possible to get some more info like type of no-clean flux you use and process parameters topside temp of board before entering the wave and dwell time in the wave. Patrick Interflux USA, Inc.
Electronics Forum | Wed Jan 27 13:55:47 EST 2010 | patrickbruneel
Randy, Thank you for the acknowledgment. The IF2005Mz is a solvent based flux (not water soluble). I agree with you that the original IF2005M had a very narrow process window. In 2000 we modified the blending procedures and blending equipment which
Electronics Forum | Fri Feb 22 09:41:54 EST 2013 | patrickbruneel
Pete, It would even be better if the wave machine manufacturers would add a feature that allows the wave to drop in rpm when a board passed the wave, and slowly get the wave back to normal rpm when a new board approaches. This would be like a reset
Electronics Forum | Thu May 31 10:52:31 EDT 2007 | patrickbruneel
A solder wire classified as L0 under IPC J-STD-004 means that the flux residues can be left on the board safely, and when you select this type of cored wire the intention is not to clean. You just select a solder wire that gives you an acceptable lev
Electronics Forum | Fri Feb 19 12:58:33 EST 2010 | patrickbruneel
Loco, If after reading these articles you still don’t believe Toyota went lead free let me know. Toyota developed their own lead free alloy http://sciencelinks.jp/j-east/article/200016/000020001600A0589899.php Quote” Several engineers are readyin