Electronics Forum | Wed Jan 18 16:30:30 EST 2006 | davef
380SR-flux gel is sold by Cobar. Look here: http://www.lumileds.com/pdfs/AB10.PDF This application note suggests: * �#1;Metals 390DH4 * �#1;Metals LR735 * �#1;Metals NS4029 * ESP 6#1;412 * Cobar 380SR#1;flux gel Comments are: * "�#1;Metals" is "A
Electronics Forum | Mon Sep 18 19:58:10 EDT 2000 | Dave F
broad answer. There's tons of suppliers. Go to "Circuit Assembly" magazine web site and look-up flux suppliers in the "Buyers Guide." Broad line suppliers are Kester, Alpha ... They will make you answer: I'm joining bla, bla, bla metals, using b
Electronics Forum | Mon Mar 29 09:33:37 EST 1999 | Chrys Shea
| I require some feed back from any one who knows about using a voc free flux in a nitrogen wave solder machine soldering both through hle and smt componants. | What disadvantages are there when using this flux? | Do you have any contact details with
Electronics Forum | Tue Mar 30 08:11:27 EST 1999 | George Steele
| | I require some feed back from any one who knows about using a voc free flux in a nitrogen wave solder machine soldering both through hle and smt componants. | | What disadvantages are there when using this flux? | | Do you have any contact detail
Electronics Forum | Mon Apr 05 08:25:31 EDT 1999 | ADRIANO FERNANDES
| | | I require some feed back from any one who knows about using a voc free flux in a nitrogen wave solder machine soldering both through hle and smt componants. | | | What disadvantages are there when using this flux? | | | Do you have any contact
Electronics Forum | Sun Feb 27 13:42:44 EST 2005 | pmdeuel
So true, We had paste flux supplied to us from Alpha metals. It was the same as used in the solder paste. The major problem we noted was the in ability to control the ratio of paste to flux resulting in lots of voids. When we mixed enough to get the
Electronics Forum | Fri Aug 01 12:35:54 EDT 2003 | blnorman
Kester recommends that we store our 1400 gm tubes on the tip. Our documentation is based on their recommendation. The Alpha past we used was stored horizontally, but that was because the flux readily separated from the metal.
Electronics Forum | Wed Apr 14 05:44:36 EDT 2004 | hun
Hi All, Just have a share with you guy. We are using T4 solder paste and also E-Stencil. We ahd try out Alpha, Kester, AIM and Qualitek. The result show Alpha had a very very heavy stack flux and can't get it clean off even by chemical
Electronics Forum | Thu May 26 08:52:42 EDT 2011 | davef
Phil Zarrow wrote a useful paper that could help in evaluating paste. Here read it ... Evaluating Solder Paste � Not An Option Contributed by Phil Zarrow of ITM an Independent SMT consulting firm With soldering being the dominant source of assembly
Electronics Forum | Tue May 11 10:43:37 EDT 2004 | Melissa
Has anyone experienced problems lately with excess flux residue left on the board after reflow when using Alpha UP78 OSP paste? We are getting a component failure that the designers are blaming on too much residue. Thanks