Electronics Forum | Mon Jan 17 02:02:38 EST 2000 | PC
Can anyone there please tell me what can cause the SMt chip terminal lifted? This happen quite often and I can't find the rootcause for this problem. Does it cause by material/Placement?? Thanks
Electronics Forum | Mon Dec 09 16:05:22 EST 2019 | slthomas
All termination platings are not created equal (sic). Some parts put up more of a fight against wetting than others, and in those cases you really have to dial it in. It seems like that in most of those cases I end up reducing the temps in the midd
Electronics Forum | Wed Jan 19 02:00:36 EST 2000 | erico
Hi wolfgang, I think Pc is not talking about the tombstone cause this terminal lifted is different from tombstone. The terminal of chip is still there but can not be solder anymore so we have to replace the chip. I also facing this problem. So can yo
Electronics Forum | Tue Oct 05 02:57:41 EDT 2010 | patejl
Reese is right. We use algorithm our AOI but the make it find liftead lead on qfp or such... it took me all day to set program and even then some defects pass so that is why Im asking..
Electronics Forum | Thu Jan 20 11:20:28 EST 2000 | Brian W.
It sounds like what you are seeing is leaching of the end cap. You need to check the manufacturer's spec. Many components have terminal barriers, which get a solder plating. Sometimes this plating process is not done well, and the solder plating le
Electronics Forum | Wed Jan 26 01:25:37 EST 2000 | erico
Hi guys, Thanks for help. It really help.
Electronics Forum | Thu Jan 20 11:16:51 EST 2000 | Wolfgang Busko
Erico:I can�t even imagine what this line looks like and what it has to do with the soldering problems without having a look at it. Also the restriction to touchup only is somewhat irritating to me. The only thing that I can think of is that in your
Electronics Forum | Wed Sep 29 05:30:59 EDT 2010 | patejl
Hi We have a problem here in the company with AOI system, most of the problem is lifted lead on qfp components.We are using SAKI BF-planet-x. Most of the defects like mising components 603 or 402 are no problem but if it comes to lifted lead even
Electronics Forum | Thu Jan 20 02:36:29 EST 2000 | erico
Hi wolfgang,Dave & PC: What I facing are: 1. The component lie flat on the board but only one side can get solder.The pad is ok, problem is with the chip. 2.I desolder the chip and go to view it under microscope and found that there is a line near t
Electronics Forum | Mon Jan 17 04:25:50 EST 2000 | Wolfgang Busko
PC: I guess you talk about something called tombstoning. About causes and adequate countermeasures you will find enough material when you browse the archive with this search item. Try also "tombstone". Good luck Wolfgang