OK, OK. 672 ball BGA. The pcbs are PC Card bus size and are .015 thick. There are 3 on a panel with about 1/2" between and rails. The aluminum plates are about 3" by 7". There are 3 cutouts which allow for the parts from either side to protrude du
Electronics Forum | Tue Jul 28 17:23:58 EDT 1998 | Robert Steltman
| | We are about to run our first BGA devices and would appreciate some confirmation on a few points. | | First some details: | | PCB & Device: | | ============= | | 1) 16 layer (4 power, 4 gnd, 8 signal) | | 2) gold on nickel finish | | 3) ceramic
Electronics Forum | Tue Jul 28 09:15:49 EDT 1998 | Justin Medernach
| We are about to run our first BGA devices and would appreciate some confirmation on a few points. | First some details: | PCB & Device: | ============= | 1) 16 layer (4 power, 4 gnd, 8 signal) | 2) gold on nickel finish | 3) ceramic BGA with eutec
Electronics Forum | Tue Feb 19 12:28:26 EST 2019 | slthomas
Presumably you're talking about lead free, but you don't say. Heller can probably provide you with a starting point, as rob has already pointed out, but you do need to develop the capability to perform profiling yourself. That oven should have ECD
Electronics Forum | Tue Oct 09 20:27:13 EDT 2001 | davef
That�s a 672 BALL BGA, bud!!! It�s a BIG Mutha!!! [I know. I know. For some reason suppliers call balls "pins".] Let�s focus on: * Clarifying the units on your PCB and aluminum plate thickness measurements. * Describing your use of the aluminum pl
Electronics Forum | Thu Oct 11 22:25:50 EDT 2001 | davef
Bruce I�m with yall. Designers and fabricators say �pins�. You say: * BGA pins are 1mm [0.039�] pitch. * BGA pads are 0.4mm [0.0157�] diameter. * BGA pins are 0.6 mm [0.024�] side-to-side. * Board thickness is ~0.4 mm [0.015�] First, as you can
Electronics Forum | Tue Jul 11 12:59:26 EDT 2006 | mattkehoe@sipad.com
We are trying to apply solder to boards with 80 microinches of electro plated hard gold. No components involved, just print 63/37 paste and reflow. The results are very poor on some boards, not so bad on others? Pictures at http://www.sipad.net/thick
Electronics Forum | Mon Jun 13 04:26:00 EDT 2005 | Joris Groot koerkamp
For the lead free reflow process we tested with our Vitronics 500smr oven. To reach the high temperature of the lead free profile was no problem. We are not using an active cooling system so the pcb's are maby to hot wen the leaving the oven. Can an
Electronics Forum | Mon Jul 27 13:59:11 EDT 1998 | Robert Steltman
We are about to run our first BGA devices and would appreciate some confirmation on a few points. First some details: PCB & Device: ============= 1) 16 layer (4 power, 4 gnd, 8 signal) 2) gold on nickel finish 3) ceramic BGA with eutectic balls Refl
Electronics Forum | Tue Jul 28 02:22:59 EDT 1998 | Bob Willis
Here is what I would do faced with your problem. First I would profile a similar board or use an existing profile. From there I would place the dummy device on the surface of a sample board with a thin thermocouple soldered to the board surface under
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830