Electronics Forum | Thu May 22 14:16:40 EDT 2003 | MikeF
We need more information to give you a good answer. Is this a leaded part (axial or radial) or smt? How big is the part, how much weight per lead? What is the end use environment, will it see any vibration? or temperature extremes? Some general com
Electronics Forum | Tue Jan 08 17:33:26 EST 2002 | davef
You didn�t identify the type of tape you use, but Kapton or similar tape is not an effective method for attaching thermocouples. Search the fine SMTnet Archives for alternatives and comparison of methods. Two methods for mechanically attaching ther
Electronics Forum | Mon Aug 19 20:45:31 EDT 2002 | davef
Bob Willis and Phil Zarrow have had a running commentary on the ability of reflowed solder to hold components on the bottom side during reflow. You can find references to their component weight to pad area rations in the fine SMTnet Archives. The
Electronics Forum | Sat Dec 27 12:30:40 EST 2008 | dmeister
Hi, Does anyone know how to determine the adhesive force of solder paste - specifically the ability of the paste to hold a component in place as it moves down the conveyors on an SMT line. Thanks, DM
Electronics Forum | Thu Dec 07 14:28:25 EST 2006 | russ
Bad design if you have to have a perfect 1206 part. you will always have a lift of some sort when reflow soldering. Solder is 3 dimensional, therefore you cannot get any underneath component, thus eliminating the automated SMT process. Cannot glue
Electronics Forum | Thu May 07 12:29:17 EDT 1998 | Rob Williams
I am running a board that is .062" thick and has components that over hang the edge of the board by .090". I have bottom side smt components (chip caps and resistors only) and use the turbulent wave to help solder the components. The problem I am h
Electronics Forum | Mon Apr 16 18:49:40 EDT 2012 | tris101
Hi guys, I'm looking for some tooling parts and I hope you can point me in the right direction. We design basic in house reflow Carriers to surport boards during reflow. I would like to add clamps to our designs but I can not locate any off the she
Electronics Forum | Wed May 06 19:51:46 EDT 1998 | D.Lange
| Dear Freinds, | DOES ANY ONE OF YOU WILL BE KIND ENOUGH TO GIVE SOME INPUT ON DOUBLE SIDE REFLOW OF COMPONENTS WHAT ABOUT BOTTOM SIDE COMPONENT HOLDING DURING 2ND SIDE REFLOW? ANY IDEA OTHER THAN USING SLDERPASTE WITH OFFSET MELTING POINT, EPOXY DI
Electronics Forum | Wed Jul 07 14:14:03 EDT 1999 | Dave F
| Is anyone aware of some guidelines regarding through-hole in SMT pads? One of our designers wants to add through-hole leads in some SMT pads for an inductor. The size of the hole is 0.032 inches and takes-up approximately 25% of the pad area. Th
Electronics Forum | Thu May 07 21:25:56 EDT 1998 | D.Lange
| I am running a board that is .062" thick and has components that over hang the edge of the board by .090". I have bottom side smt components (chip caps and resistors only) and use the turbulent wave to help solder the components. The problem I am
Main Products: 1. Original new and Original Used SMT/AI Spare Parts. 2. SMT Equipments And Related Machine( SMT Calibration, SMT Feeder Carts,Conveyer etc.) 3. Maintenace and Repair Service Pre-Sales Service Provide details ab