We got a similar alloy Sn05Pb93.5Ag1.5, of Alpha Vaculoy bars. It is not the eutectic alloy you were looking for but it is close. This alloy and similar high temperature alloys are used in downhole electronics and so a supplier in the Houston area
Electronics Forum | Fri Feb 17 14:11:32 EST 2012 | tkotwal
I'm also looking for tips for SMT hand soldering with Sn05Pb93.5Ag1.5. Our technician is quite good with standard SMT hand soldering, but hasn't worked with HMP solder. Some specific questions: - If the iron tip is hot enough (consistently), can we
Electronics Forum | Fri May 14 00:34:22 EDT 1999 | Mike D.
| I need some pics or documentation on how a finish soldered joint looks like for SMT component. I have various people who supposedly says has knowledge with High Temp says my joint could look better. The joint looks shiny and great except for a grai
Electronics Forum | Tue Aug 23 16:48:29 EDT 2011 | jax
assuming Sn05Pb93.5Ag1.5 Without knowing what you are trying to solder, PTH or SMT, the time might not be that far off. Does that time include stripping, cleaning, plating the leads prior to soldering onto the board?... pre-tinning the board as well
Electronics Forum | Tue Sep 11 21:24:00 EDT 2012 | vergara1
I'm also looking for tips for SMT hand soldering > with Sn05Pb93.5Ag1.5. Our technician is quite > good with standard SMT hand soldering, but hasn't > worked with HMP solder. > > Some specific > questions: > > - If the iron tip is hot enough >