Electronics Forum | Sat Nov 08 10:04:26 EST 2003 | severs
Once you have selected your plating based on electrical and physical requirments, you should know that there is an inexpensive plastic storage packaging developed by Lucent which can keep any platings solderability from degrading for up to 10 years o
Electronics Forum | Mon May 09 09:02:17 EDT 2005 | davef
Your 316L stainless steel pot will not contain lead-free solder, over the long term. We'd bet that our solder machine equipment manufacturer will "swap" you a lead-free solder compatable pot for your current pot.
Electronics Forum | Sat May 07 04:40:04 EDT 2005 | grayman
Hi, There are many companies shifting lead free solder wave. My question is can anyone give me idea if we can still use our old solder wave machine for lead free eventhough the solder pot is stainless steel 316L? Our solder bath has titanium nozzl
Electronics Forum | Wed Jun 29 03:37:53 EDT 2005 | lupo
Hi, I think that the time depends on the type of stainless steel, temperature and solder alloy. For example, one of our machines is delivered with 316 stainless pot and alloy SnNi. It worked six months (120days*16hours = 1920hours) and aft
Electronics Forum | Fri Jul 08 09:57:31 EDT 2005 | fctassembly
Proy, Another issue is what exact formulation of SAC is used. Much of the SAC305 being used in Asia contains phosphorus, which is added in an attempt to reduce the heavy drossing that SAC305 produces. Phosphorus acts as a flux on steel so will increa
Electronics Forum | Tue Dec 23 11:55:37 EST 2003 | Marc Simmel
Details, details: 1) The metal shell is part of the component body. The base metal is austenitic stainless steel (304) that has been plated with 90/10 tin-lead over nickel (semi-bright). 2) The entire part (leads and shell) is elevated by the mass o
Electronics Forum | Tue Nov 24 18:54:36 EST 2009 | gregoryyork
Some companies claimed their lead free solders wouldnt attack stainless steel, frankly they do and they should not be allowed to get away with these claims. Lead Free does not attack Cast iron
Electronics Forum | Thu May 26 08:52:42 EDT 2011 | davef
Phil Zarrow wrote a useful paper that could help in evaluating paste. Here read it ... Evaluating Solder Paste � Not An Option Contributed by Phil Zarrow of ITM an Independent SMT consulting firm With soldering being the dominant source of assembly
Electronics Forum | Mon May 16 18:03:30 EDT 2005 | davef
Key Issue: Will this machine solder your boards? You never know until you solder one. Any other avenues of analysis involve substantial risk. Flux Selection * High or low solids * VOC or VOC-free Solder Alloy * If using lead-free, avoid stainles
Electronics Forum | Mon Nov 07 06:25:26 EST 2005 | Adnahn
Please advise if Plasma Nitride for Stainless Steel is suitable or a proposed method to coat the wave solder bath for leadfree. Thanking you in advance. Regards, Adnahn