Electronics Forum | Tue Sep 21 13:10:10 EDT 1999 | Dave F
| Dear All, | | In order to understand the soldering technologies in SMT, I'd like to understand why some cards are soldered and then cleaned, or only soldered whitout water cleaning nor "ultra sound" wavelength. | | I mean that I wonder why we use
Electronics Forum | Wed Sep 22 02:45:23 EDT 1999 | Brian
| | Dear All, | | | | In order to understand the soldering technologies in SMT, I'd like to understand why some cards are soldered and then cleaned, or only soldered whitout water cleaning nor "ultra sound" wavelength. | | | | I mean that I wonder
Electronics Forum | Fri May 27 11:55:37 EDT 2005 | Sarag
There is also a new cleanliness tester that looks at localized areas to provide a cleanliness reading and can extract a sample to use in ion chromatography testing. You can find out about it here: http://www.residues.com/C3.html
Electronics Forum | Fri Jun 01 12:07:53 EDT 2001 | medernach
No clean residues can range in appearance from brownish gunk that looks like tree sap (because it is in some instances) to almost no residue at all. Is this product exposed to a wave soldering process or SMT? I would guess it's a wave process if th
Electronics Forum | Thu Dec 23 03:05:26 EST 2004 | Steve Stach
The Jury is still out on no-clean reliability in the long term as no-clean didn't gain wide spread acceptance until the early 1990's. Also, in today's disposable society, few products are expected to last 15-20 years. Experience has shown that if y
Electronics Forum | Sat Dec 03 17:21:45 EST 2011 | davef
We can't tell much from your pictures, except there are rounded gray blobs that could be solder. If that's the case, you need to get that solder hotter. Please give us the temperature readings of those blobs during reflow. You mentioned that you're
Electronics Forum | Wed Nov 30 09:19:57 EST 2011 | siaomuay
Dear Shean Dalton Peak temperature 240'c and we use IPA for cleanning Pcb surface before mounting
Electronics Forum | Fri May 17 03:04:15 EDT 2002 | Mike Konrad
This conversation reminds me of the old �How Many Engineers Does It Take To�� joke. We manufacturer the ionic contamination (ROSE, SEC) testers and I am not aware of anyone that performs such exacting surface area calculations. Most people use th
Electronics Forum | Fri Jun 18 13:48:37 EDT 1999 | Earl Moon
| We currently use HASL on all of our boards and I would like to move to something else. I have sampled some boards with Entek OSP and I loved it, the problem is we have plated mounting holes on just about every board we make. Does anyone have info
Electronics Forum | Tue Aug 24 14:49:58 EDT 2004 | jamyboy
Hi, I am trying to assemble a LTCC component > with Pd/Ag surface finish on to Sn/Pb/Ag solder > and Sn/Ag/Cu solder. I am passing it through a > reflow. I have observed poor wettability at the > solder-pad joint. Does anyone have information
The SMTA membership is a network of professionals who build skills, share practical experience and develop solutions in electronic assembly technologies and related business operations.
Training Provider / Events Organizer / Association / Non-Profit
6600 City W Pkwy
Eden Prairie, MN USA
Phone: 952-920-7682