Electronics Forum | Fri Feb 26 14:36:58 EST 2010 | gregp
Hi Dave, The short answer is "it doesn't". The mascot is simply a light guided assembly system. The major difference is the CS-400E machine has the fully programmable cut and clinch unit doing it's thing under the board while it is being assembled.
Electronics Forum | Fri Feb 12 12:19:28 EST 2010 | rodrigo
What do you mean by "check if F4G is connecting to CC...". The CC DOS windows shows up when I login the PC so does the remote shell daemon. The CC DOS windows says a bunch of stuff does has been woken. I didn't install the FTP stuff. I didn't think I
Electronics Forum | Sun Feb 14 15:43:32 EST 2010 | jlawson
ERP/ MRP systems can do basic traceability but often fall through as make a lot of asumptions and can not capture realtime info and account for all possible situations. I have seen alot of companies do this and there is always a 'shoe horned' system.
Electronics Forum | Thu Apr 01 03:44:31 EDT 2010 | nico67640
Good Morning Nicolas, > > Per J-STD-033B, 5.3.3.2 > states that a Dry cabintet maintained at not > greater than 5% RH may be considered MBB > storage. > > Hope this helps > > Chris Thanks Chris for your answer. I'm ok with you about the per
Electronics Forum | Fri Apr 02 12:41:12 EDT 2010 | CL
Nicolas, 4.1.2.1 and 4.1.2.2 mention the requirements for drying an MSD to resett the clock life. 4.1.2.2 states that once a component is dried, refer to 5.3 for safe storage. Under that specification is 5.3.3.2 DRY Cabinet at 5% RH- This states tha
Electronics Forum | Fri Feb 19 12:58:33 EST 2010 | patrickbruneel
Loco, If after reading these articles you still don’t believe Toyota went lead free let me know. Toyota developed their own lead free alloy http://sciencelinks.jp/j-east/article/200016/000020001600A0589899.php Quote” Several engineers are readyin
Electronics Forum | Mon Mar 01 10:36:55 EST 2010 | patrickbruneel
Loco, Since Dave didn't respond i will. We shouldn't forget that even when using tin/lead solder the boards and components are still lead free. Parts that are not completely wetted by the tin/lead solder still have the potential for tin whiskering a
Electronics Forum | Wed Feb 17 12:16:17 EST 2010 | dcell_1t
Hi there: During the past weeks (let's say since beginning of the year) we've been experiencing some issues with shifted components. We verify for position before Reflow oven and the components are Ok, but they observe shifted after reflow. it occurs
Electronics Forum | Fri Feb 26 08:30:10 EST 2010 | davef
Low cost prototyping * TWS Automation Quadra [www.tws-automation.com 39 0585 634758] * Versatronic RV4 [VSMT Solutions Ltd; 6 Dean Way, Aston Clinton, Aylesbury HP22 5GB, Buckinghamshire; 01296 630341 F01296 632144 http://www.vsmt.co.uk; David Clemen
Electronics Forum | Fri Mar 19 09:00:18 EDT 2010 | jorge_quijano
Just a comment, we have been using the OEE as metric in our plant, what I've seen is that can be misunderstood because a good OEE level does not mean a good machine utilization, let me try to explain this on my own words. I have a HMLV line, so when
.gif)