Electronics Forum | Fri Nov 11 04:13:23 EST 2005 | arnold
we are manufacturer of molded type transformer and we soldered are units using wave soldering machine and then we washed the units to remove flux residue. what materials or any process for us to eliminate the process of washing after wave soldering.
Electronics Forum | Fri Jan 23 09:21:22 EST 2009 | sm2009
Hello, thanks to everyone that reply to my previous question. I have another request: is it possible to solder polyester capacitors (case 2220) with wave soldering process? Thanks! Regards, Stefano
Electronics Forum | Thu Jan 29 12:57:37 EST 2009 | wavemasterlarry
Only if it has exposed ends on the end.
Electronics Forum | Mon May 07 22:00:11 EDT 2007 | seb1970
what type of preheater does the novastar use and what temp. is it set on? I am also use to a hollis wave solder machine. Old and crude but works great.
Electronics Forum | Mon May 14 08:53:42 EDT 2007 | realchunks
Can't do much better than Electrovert. http://cgi.ebay.com/SPEEDLINE-ELECTROVERT-ULTRAPAK-445-16-WAVE-SOLDER-MACH_W0QQitemZ220111865148QQihZ012QQcategoryZ58293QQssPageNameZWDVWQQrdZ1QQcmdZViewItem
Electronics Forum | Mon Feb 23 05:37:23 EST 2009 | emmanueldavid
Necoleta, PWB Blistering/De-lamination may not be due for Titanium finished threads / holders which is typically being used to draw high Shelf Life of Pallets and even flow across Auto Wave Soldering rails. There is also nothing to suspect on Liquid
Electronics Forum | Fri Jan 28 12:30:57 EST 2005 | glenda
We are looking for a used or new wave machine must be able to do lead free solder. Does anyone have contact information in the Chicago, il area for used wave soldering machines? Thanks for any help we can get.
Electronics Forum | Tue Jul 24 03:26:45 EDT 2001 | winnifred
Dr. Lee, For lead-free wave soldering, we are recommended to use SnCu0.7, why not 0.8 or more ?? Since SnCu0.7 has eutectic melting point at 227 deg C, does it mean with more Cu or less Cu, the melting point will be higher ?? Also, in lead solderin
Electronics Forum | Fri Jun 12 11:15:50 EDT 1998 | Ryan Jennens
Hey all! The wave solder warrior is back. I have found a flux which leave almost no residue (the least yet), but because of its super low solids content I absolutely cannot get topside fillets. The multi-layer, two sided board is on a pallet w
Electronics Forum | Mon May 07 15:08:09 EDT 2007 | davef
What is a smart way to determine that the solder in the wave pot is moving at the same speed as the board?