Electronics Forum | Sat Sep 20 07:11:28 EDT 2008 | Sean
Hello All, I used to hear that PCB with immersion silver finishing, its non component location pads, tend to be discolour (Yellowish) after went through heat cycle, such as reflow oven. However, if the component solderbility on the PCB is OK, can w
Electronics Forum | Mon Sep 05 01:38:12 EDT 2005 | plcc
I hv a PCB (mtrl is RF35). After going thru' reflow, we found yellowish stain on the solder pad (solder mask). It looks like burn-marks. The reflow temp use is 245oC. We tried running bare pcb under 220oC, there's minimum stain found (acceptable),how
Electronics Forum | Wed Sep 16 00:03:55 EDT 2009 | linseeg
We encoutered few PCB after IR reflow the PCB pad change color from silver to yellowish / brownish. Our IR reflow peak temp is ~250 degree. The brownish cannot be remove with IPA as well. What is the main reason causing this issue?
Electronics Forum | Thu Sep 28 07:57:58 EDT 2006 | cpm
Hi, Expert, Currently, I'm facing a very critical problem on my HAL leadfree finishing PCBs at my customer end. We run the HAL leadfree (Tin, cu and ni) board by using HAL leadfree machine (temperature about 270 deg.C) and go for normal water post c
Electronics Forum | Sun Jan 25 17:40:16 EST 2009 | cuperpeter
Hello All, I have a problem with nonwetting Au finish after second cycle of reflow soldering doublesided boards. Solder nonwetted pcb pads (is wicked to component terminations) Either these pads or some of non component pads became discoloured from
Electronics Forum | Tue Feb 03 16:42:50 EST 2009 | cuperpeter
Hello All, > > I have a problem with nonwetting Au > finish after second cycle of reflow soldering > doublesided boards. Solder nonwetted pcb pads (is > wicked to component terminations) Either these > pads or some of non component pads became
Electronics Forum | Wed Dec 19 01:17:13 EST 2001 | ianchan
Hi Experts, I need help here, advice appreciated from all... Production is running a Lot of flex-circuit PCB, through the SMT line, with 0402 components. The flex-PCB is taped to FR4 support "pallets" when processing thru' the SMT P&P m/c. We use
Electronics Forum | Tue Oct 03 17:04:07 EDT 2006 | cuculi54986@yahoo.com
Glenn, What alloy are you using for Pb-free HASL? You say tin copper nickel, but is it SN100C? Against manufacturing engineering's recommendation, my company specified simply "Pb-free HASL" as the finish for our Pb-free PCBs. One of our suppliers
Electronics Forum | Wed Aug 22 22:22:52 EDT 2001 | davef
First an administrative point, you can edit the postings that you make on SMTnet. Look for the yellowish-greenish EDIT button at the top of your posting. Second there are over 170 postings on intermetallic* on the fine SMTnet Production Forum Archi