| https://www.eptac.com/faqs/soldertips/soldertip/soldertips-issues-with-incomplete-solder-reflow-in-production-2
becoming totally molten and coalesce forming a homogeneous molten solder volume. If the solder paste appears to not have reflowed and is as identified in IPC-A-610 section 5, the issue is that the proper intermetallic has not formed at both the component and pad/land surface
Heller Industries Inc. | https://hellerindustries.com/wp-content/uploads/2018/07/pan_APEX06.pdf
SnPb solder joints is higher than that of SAC305 solder joint because the wetting of SnPb is better than that of SnAgCu. Figure 14. Cross-section View of SnPb Solder Joint Reflowed at 215C for 90 sec. Figure 15. Cross-section View of SAC305 Solder Joint
Heller Industries Inc. | https://hellerindustries.com/wp-content/uploads/2022/04/pan_APEX06-1.pdf
SnPb solder joints is higher than that of SAC305 solder joint because the wetting of SnPb is better than that of SnAgCu. Figure 14. Cross-section View of SnPb Solder Joint Reflowed at 215C for 90 sec. Figure 15. Cross-section View of SAC305 Solder Joint
| https://www.eptac.com/faqs/ask-helena-leo/ask/post-lead-trimming-reflow-requirements
: This following information is from Rev D of IPC-A-610. The requirement was to inspect all joints after cutting and make a determination as to whether or not the connection was damaged, then if damage was found, the solder joint was to be reflowed
| https://www.eptac.com/wp-content/uploads/2021/11/webinar_eptac_12_17_08.pdf
| http://etasmt.com/cc?ID=te_news_bulletin,14961&url=_print
. The bottom component of the large board is easily dropped during the second reflow process, or the bottom solder joint is partially melted, causing solder joint reliability problems
| https://www.eptac.com/faqs/ask-helena-leo/ask/j-std-001f-vs-space-addendum
: We were looking over the J-STD-001 and the Space Addendum requirements for partially visible or hidden solder connections 4.18.3. Why does the space addendum give you the option to x-ray the parts in Note D, but in the J-STD-001 book
| https://www.eptac.com/ask/j-std-001f-vs-space-addendum/
: We were looking over the J-STD-001 and the Space Addendum requirements for partially visible or hidden solder connections 4.18.3. Why does the space addendum give you the option to x-ray the parts in Note D, but in the J-STD-001 book there is no option for inspection if you
| https://www.eptac.com/wp-content/uploads/2012/09/eptac_10_17_12.pdf