Electronics Forum | Mon Mar 29 09:33:37 EST 1999 | Chrys Shea
| I require some feed back from any one who knows about using a voc free flux in a nitrogen wave solder machine soldering both through hle and smt componants. | What disadvantages are there when using this flux? | Do you have any contact details with
Electronics Forum | Tue Mar 30 08:11:27 EST 1999 | George Steele
| | I require some feed back from any one who knows about using a voc free flux in a nitrogen wave solder machine soldering both through hle and smt componants. | | What disadvantages are there when using this flux? | | Do you have any contact detail
Industry News | 2011-01-20 13:45:14.0
IPC will introduce a cyber conference at IPC APEX EXPO in Las Vegas in 2011. The IPC APEX EXPO Cyber Conference will feature live broadcasts and post-show archives of seven of the show's thirty-five technical conference sessions on April 12–14, 2011.
Industry News | 2018-06-03 19:11:33.0
SHENMAO America, Inc. is exhibiting at the 2018 IEEE 68th Electronic Components and Technology Conference (ECTC), taking place May 29 - June 1, 2018 at the Sheraton San Diego Hotel & Marina. SHENMAO plans to showcase its new PF906-S and PF912-S solder alloys, and SMF-WC53 Water-Soluble / Cu-OSP Pad Ball Attach Flux.
Technical Library | 2021-10-20 18:21:06.0
The solderability of the SAC305 alloy in contact with printed circuit boards (PCB) having different surface finishes was examined using the wetting balance method. The study was performed at a temperature of 260 _C on three types of PCBs covered with (1) hot air solder leveling (HASL LF), (2) electroless nickel immersion gold (ENIG), and (3) organic surface protectant (OSP), organic finish, all on Cu substrates and two types of fluxes (EF2202 and RF800). The results showed that the PCB substrate surface finish has a strong effect on the value of both the wetting time t0 and the contact angle h. The shortest wetting time was noted for the OSP finish (t0 = 0.6 s with EF2202 flux and t0 = 0.98 s with RF800 flux), while the ENIG finish showed the longest wetting time (t0 = 1.36 s with EF2202 flux and t0 = 1.55 s with RF800 flux). The h values calculated from the wetting balance tests were as follows: the lowest h of 45_ was formed on HASL LF (EF2202 flux), the highest h of 63_ was noted on the OSP finish, while on the ENIG finish, it was 58_ (EF2202 flux). After the solderability tests, the interface characterization of cross-sectional samples was performed by means of scanning electron microscopy coupled with energy dispersive spectroscopy.
Technical Library | 2021-08-25 16:28:36.0
In this study, a Sn–Bi composite solder paste with thermosetting epoxy (TSEP Sn–Bi) was prepared by mixing Sn–Bi solder powder, flux, and epoxy system. The melting characteristics of the Sn–Bi solder alloy and the curing reaction of the epoxy system were measured by differential scanning calorimeter (DSC). A reflow profile was optimized based on the Sn–Bi reflow profile, and the Organic Solderability Preservative (OSP) Cu pad mounted 0603 chip resistor was chosen to reflow soldering and to prepare samples of the corresponding joint. The high temperature and humidity reliability of the solder joints at 85 #14;C/85% RH (Relative Humidity) for 1000 h and the thermal cycle reliability of the solder joints from
Events Calendar | Tue Apr 13 00:00:00 EDT 2021 - Tue Apr 13 00:00:00 EDT 2021 | ,
Boston Chapter Webinar: Cleaning Chemistry For PWB and Rework - Part 2, session 1
Events Calendar | Tue Apr 13 00:00:00 EDT 2021 - Tue Apr 13 00:00:00 EDT 2021 | ,
Boston Chapter Webinar: Cleaning Chemistry For PWB and Rework - Part 2, session 2
Heller Industries Inc. | https://hellerindustries.com/wp-content/uploads/2022/06/Vacuum-Fluxless-Reflow-Technology-for-Fine-Pitch.pdf
: contact angle of Sn wetting on Cu; H: solder bump height; D: bump diameter dimension, as well as flux agent wetting force. In this study, our focus is mainly on oxide removal agent wetting
Surface Mount Technology Association (SMTA) | https://www.smta.org/icsr/speaker_forms/Paper-Format-Requirements.doc
experiments in this study were performed on an OSP finished board. Finishes such as OSP which do not have a nickel later represent the worst case scenario with respect to Cu dissolution. An OEM server product was used as the test vehicle throughout this study