Electronics Forum | Mon Jan 24 06:19:04 EST 2011 | fönsi
Hello! I've had the same problem about one Jear ago. We had exessive building of voids in the solder joints. I recomment to take a pincer to break off some of the components. If the solder joint is good, the copper pad will stay at the solder joint
Electronics Forum | Thu Jan 13 17:46:04 EST 2011 | davef
We've never seen the defect that you describe, but in wave soldering-land blowholes usually are caused by moisture in the board that out-gasses through the too thin plating of through holes. * Bandaid fix: bake the boards * Long-term fix: Obtain boar
Industry News | 2015-05-18 21:19:33.0
The SMTA Capital Chapter is pleased to announce it will welcome Denis Barbini, Universal Instruments Corporation, on June 9th to instruct a tutorial on Advanced SMT Technologies at ZESTRON Americas located at 11285 Assett Loop, Manassas, VA 20109. The tutorial is scheduled from 9:00 am to 4:30 pm and includes lunch. The following should attend: quality engineers, failure analysis engineers, reliability engineers, procurement specialists, design engineers, process engineers, project managers. Registration is required for this learning event.
Industry News | 2018-10-18 09:14:05.0
Lead-free processes propose new requirements on reflow soldering quality
Parts & Supplies | Pick and Place/Feeders
Many companies first applied SMT second-hand placement machines, and the selected placement machines were relatively stable, with low failure rate, easy maintenance, and important maintenance costs. Therefore, there are still many concerns about buyi
Parts & Supplies | Pick and Place/Feeders
Many companies first applied SMT second-hand placement machines, and the selected placement machines were relatively stable, with low failure rate, easy maintenance, and important maintenance costs. Therefore, there are still many concerns about buyi
Technical Library | 2023-01-17 17:27:13.0
Reflow profile has significant impact on solder joint performance because it influences wetting and microstructure of the solder joint. The degree of wetting, the microstructure (in particular the intermetallic layer), and the inherent strength of the solder all factor into the reliability of the solder joint. This paper presents experimental results on the effect of reflow profile on both 63%Sn 37%Pb (SnPb) and 96.5%Sn 3.0%Ag 0.5%Cu (SAC 305) solder joint shear force. Specifically, the effect of the reflow peak temperature and time above solder liquidus temperature are studied. Nine reflow profiles for SAC 305 and nine reflow profiles for SnPb have been developed with three levels of peak temperature (230 o C, 240 o C, and 250 o C for SAC 305; and 195 o C, 205 o C, and 215 o C for SnPb) and three levels of time above solder liquidus temperature (30 sec., 60 sec., and 90 sec.). The shear force data of four different sizes of chip resistors (1206, 0805, 0603, and 0402) are compared across the different profiles. The shear force of the resistors is measured at time 0 (right after assembly). The fracture surfaces have been studied using a scanning electron microscopy (SEM) with energy dispersive spectroscopy (EDS)
Technical Library | 2018-11-20 21:33:57.0
There are several industry-accepted methods for determining the reliability of flux residues after assembly. The recommended methods of test sample preparation do not always closely mimic the thermal cycle experienced by an assembly. Therefore, extraction from actual assemblies has become a popular method of process control to assess consistency of post-reflow cleanliness. Every method of post-reflow flux residue characterization will depend on the reflow process followed to prepare the coupon.This investigation will focus on the effect of thermal conditions on the remainder of active ingredients in flux residues after assembly with no-clean solder pastes.
EKT AOI machine application: inspection after stencil printing, pre/post reflow oven, pre/post wave soldering?FPC etc. Stencil printing: Solder unavailability, insufficient or excessive solder, solder misalignment, bridging, stain, scratch etc. Compo
SMT Express, Volume 4, Issue No. 5 - from SMTnet.com Volume 4, Issue No. 5 Thursday, May 23, 2002 Featured Article Return to Front Page Book Review Reviewed by Dave Fish (davef ), Pandion Electronics, Inc. Title: Reflow Soldering
| http://etasmt.com/cc?ID=te_news_bulletin,8362&url=comment
Nitrogen reflow oven | I.C.T After-sales Service-News-Reflow oven,SMT Reflow Soldering Oven-cmsadmin Home About I.C.T News Products Video Projects Service Join Us Contact Us Home About I.C.T
Heller 公司 | http://hellerindustries.com.cn/Vacuum-Void-Reduction-Reflow.pdf
The Effect of Vacuum Reflow Processing On Solder Joint Voiding And Thermal Fatigue Reliability To be published in the Proceedings of SMTA International, September 17 - 21, 2016, Rosemont, IL
COT specializes in high quality SMT nozzles and consumables for pick and place machines. We provide special engineering design service of custom nozzles for those unique and odd components.
2481 Hilton Drive
Gainesville, GA USA
Phone: (770) 538-0411
.png)