Electronics Forum | Wed Feb 27 04:23:13 EST 2008 | fujillews
Hi It is best to fit the VGA camera for 0201 parts make sure your software is high enough..above v1.33 although you can place without but no so good. 0.4mm tapered nozzles are best. 0201 feeder the locator base in increased by aprox 0.3mm and the ind
Electronics Forum | Fri Feb 22 10:27:03 EST 2008 | fastek
Well I've heard you must get the 0201, 0.4mm tape feeder to place an 0201 component as the 0402 feeder won't do it. They ain't cheap @ $1,000 each from Fuji roughly. Also you will need to get 0.4mm nozzles on your machine. Have you actually done thi
Electronics Forum | Fri Sep 02 07:38:13 EDT 2005 | DannyJ
Hi Mike, I haven't tried the 0201s with a Hyrda, but after seeing 20 reviews of your message without a response, I'll try and share my experience with 0402s on a non-Hydra machine. The 0402s are slow, but I managed to get some speed by maxing out
Electronics Forum | Fri May 12 11:27:40 EDT 2006 | bobpan
no...there is no retrofit kit.....but if you find some good feeders....tear into them.....make sure everything is tight....about half the time you can make the feeder work ok. Also it doesnt hurt to use only one xf nozzle in the program so that only
Electronics Forum | Tue Dec 13 09:29:08 EST 2011 | swag
We're soon to build a lead free assembly with 0201 components. I'm not worried about placement as our machines can handle it. Any tips on printing, screens, reflow?
Electronics Forum | Wed Jun 05 17:13:58 EDT 2002 | Yannick
Hello! I have a strage problem, we made some production with uBGA, BGA, 0201, 0805, and other type of component. We didn't put the uBGA and 0201 and BGA on the board at the end of the line we look a our solder joint and surprise the solder made a
Electronics Forum | Wed Sep 25 06:56:16 EDT 2002 | CH
U may check your profile ramp rate. The flux may evporated and look like cold joint
Electronics Forum | Wed Dec 14 11:06:12 EST 2011 | swag
Thanks, Dave. Really good article.
Electronics Forum | Mon Sep 23 18:11:10 EDT 2002 | steveb
On an assembly reflowed in air saw the same thing: 0201's with a grainular solder joint, but 0402's and above with perfectly formed joints. Reflow profile all within acceptable tolerances. Reflowing in nitrogen solves this problem, but increases t
Electronics Forum | Wed Jun 05 21:33:12 EDT 2002 | davef
Tough to say based on what you have told us. Things to Determine are: * Is the heat at the solder connections that are not reflowing properly adequate? * Is the pad surface of the solder connections that are not reflowing properly solderable?