Electronics Forum | Wed May 01 10:16:05 EDT 2002 | davef
Consider contacting Alpha Metals at http://www.alphametals.com/tech_services/index.html
Electronics Forum | Tue Apr 30 16:18:37 EDT 2002 | mantis
Can anyone tell me the difference between the these 2 fluxes as i cant find a data sheet(i searched the alpha metals website) for the E191.I know the the 2 fluxes are both no clean but other than that?? The reason i ask is i found some E191 in our st
Electronics Forum | Tue May 09 18:00:33 EDT 2006 | russ
in all actuality, you are both right. Alpha metals does have the toughest/hardest noclean residue that I have seen. When changing to no-clean FLUX you should run different probes. So back to square one. You're both right so who's gonna win?
Electronics Forum | Tue Feb 29 10:14:02 EST 2000 | Robert Hartmann
My company is just getting into the flip chip packaging arena. We are putting in a prototype/small volume wire bond PBGA line. We have some questions with regard to choosing solder balls and cleaning of flux. 1) Is there a formula for the shrink
Electronics Forum | Tue Feb 29 10:14:02 EST 2000 | Robert Hartmann
My company is just getting into the flip chip packaging arena. We are putting in a prototype/small volume wire bond PBGA line. We have some questions with regard to choosing solder balls and cleaning of flux. 1) Is there a formula for the shrink
Electronics Forum | Wed Sep 18 14:12:40 EDT 2013 | pjchonis
Hello Bachman. SAC305 is the most common lead-free solder alloy, not only for wave soldering but also selective. Most of our selective customers (especially automotive) are using SAC305. What is more important than the alloy to consider is the flux
Electronics Forum | Thu Feb 15 13:47:16 EST 2007 | russ
They are all compatible with each other. Data is at alpha metals website and FCT assembly Russ
Electronics Forum | Mon Sep 18 19:58:10 EDT 2000 | Dave F
broad answer. There's tons of suppliers. Go to "Circuit Assembly" magazine web site and look-up flux suppliers in the "Buyers Guide." Broad line suppliers are Kester, Alpha ... They will make you answer: I'm joining bla, bla, bla metals, using b
Electronics Forum | Thu Nov 17 20:51:16 EST 2005 | cangly
Morning Mike, We use Pb63/Sn37, Alpha Metal alloy. Solder pot is at 250 C. The profile of board after Preheat about 100 C, Lambda Wave about 220C (use both Lambda and Chip wave), DWell time 2.1s ~ 3s. Conveyor speed 1.5 in/min. We run by bare board a
Electronics Forum | Tue Apr 06 13:11:22 EDT 1999 | Mike Konrad
I would recommend the following chemistries: Zestron Vigon SC200... Good but very $$$$ (703) 589-1198 Vertex (sold by Petrofirm and Alpha Metals)... Won't last as long as Zestron but must less $$$ (904) 261-8286 Kyzen... Also very good (800) 84