Electronics Forum | Fri Nov 02 09:09:56 EDT 2012 | davef
Sure you can use it it with leaded HASL. Recognize that ... * Your Sn42/Bi58 will no linger be Sn42/Bi58 * Your leaded HASL will no longer be the same leaded HASL that walked in the door to your plant * Lead from HASL coatings can diffuse through the
Electronics Forum | Tue Jul 16 21:53:51 EDT 2002 | davef
We don't use Sn43Pb43Bi14 solder. We don't make high performance circuit boards that are subjected to temperatures from -55� Celsius to +85� Celsius and vibration requirments at 6g. We don't like bismuth solder alloys, because: * Fatigue life is r