Electronics Forum | Sun Dec 17 18:16:27 EST 2006 | greg york
can you describe the residue more for me cheers greg blt circuit services
Electronics Forum | Thu Oct 30 07:52:39 EDT 2008 | ccouture
Thank you Dave and BLT, very informative replies.
Electronics Forum | Tue Feb 11 14:37:26 EST 2020 | spoiltforchoice
If you're asking me, I'm using BLT LFS-UFP-T4 (they have an even better paste to treat badly now if you add zq). Those in the test of the world might find Loctite GC10 is similar, however the stencil and tack times on the BLT are pretty awesome and
Electronics Forum | Wed Jun 13 06:42:14 EDT 2012 | brettrenishaw
We have a problem with our Unleaded wave solder machine only randomly soldering some pads. I have looked at the flux level and that appears fine aswell as cheking the preheat and solder height in the bath. The probelm is not exclusive to one perticul
Electronics Forum | Wed Sep 15 07:43:11 EDT 2004 | gregoryyork
It may be worth baking the boards for an hour at 120C and then trying it straight away do not leave them lying around.Is the fillet shallow and inverted back into the board. Do you have any blow holes as well? Cheers Greg BLT
Electronics Forum | Wed Sep 29 17:59:59 EDT 2004 | gregoryyork
I would be interested in this as well. Can you forward me some details. thanks Greg York Technical Sales Manager BLT Circuit Services Ltd - UK
Electronics Forum | Wed Jan 18 17:35:08 EST 2006 | gregoryyork
We manufacture solder and dont charge, so agree with the others and change elsewhere just make sure you are changing to better material if unsure stick with what you have and pay for it under duress. Cheers Greg York BLT Circuit Services Ltd England
Electronics Forum | Mon Jan 28 06:19:30 EST 2008 | gregoryyork
Hi I would suggest Datum Dynamics using the Durostone Lead Free version pallets are very good. They dont thermally degrade as quick as others out there so dont deposit as much residue in the wave Cheers Greg BLT Circuit Services Ltd
Electronics Forum | Wed Aug 12 09:01:53 EDT 2009 | gregoryyork
Hi Can you be a little more specific with wave solder machine name and method of applying flux and if lead free or not then can come back with some meaningfull figures Cheers GREG BLT
Electronics Forum | Wed Nov 04 11:25:39 EST 2009 | gregoryyork
No Sorry it was just from memory I will try to google it and see what I can find. I know it is bad to have too thin a Nickel layer and Phos layer. If you find anything can you let me know as well Cheers GREG BLT