Electronics Forum | Fri Sep 24 20:02:39 EDT 2004 | pabloquintana
OK, We have tested and changed several things in our process, but we still getting the same result. We are trying another type of coating. We will see later. My question now is what is adhesion wise acceptable in the industry. I know many of you wi
Electronics Forum | Sat Sep 25 08:59:59 EDT 2004 | davef
IPC-HDBK-830, Guidelines for Design, Selection and Application of Conformal Coatings says: A conformal coating may have several functions depending on the type of application. The most common are: * Inhibit current leakage and short circuit due to h
Electronics Forum | Tue Sep 21 11:39:41 EDT 2004 | pabloquintana
Conformal coat a bare board to determine if there > is there is enough surface free energy from your > solder mask to prevent dewetting. Sorry for my ignorance, but what is "enough surface free energy"? How do I determine that? >* Bake a board
Electronics Forum | Thu May 28 22:12:18 EDT 2009 | davef
If your newer board passes a tape test, you should be OK.
Electronics Forum | Wed Nov 01 09:01:55 EST 2000 | Thomas Ballhausen
Since your problem has been posted quite some time ago I am eager to know, if you have got any clue. One of my customers recently claimed our 313-PBGA causing problems, as one of its balls (randomly) is almost dewetting. So no evidence is found by x-
Electronics Forum | Thu Oct 24 14:10:53 EDT 2002 | Terry Burnette
I've been informed that I can't post the Dye Penetrant paper on the SMTNET library till Advanced Packaging releases the paper in their Dec. issue. You should be able to pull a copy in the next couple of weeks from their site, http://ap.pennnet.com/ho
Electronics Forum | Tue Aug 12 09:52:58 EDT 2014 | thiagofrego
Would like to know if some exists norm that refers the parameters for test of extraction (pull test) of components SMD using adhesive.
Electronics Forum | Mon Mar 05 15:29:50 EST 2007 | ck_the_flip
When no-clean flux and no-clean soldering first came out in the late 80's / early 90's, there were lots of White Papers written about conformal coating adhesion and no-clean flux. I'm pretty sure all CC's will adhere to today's chemistries. To be o
Electronics Forum | Sat Feb 14 19:35:51 EST 1998 | C. Lao
Mr Lao We have some specialist knowledge on this subject and offer both equipment and services for these tests. My first recommendation is that take coupons manufactured by your PC Fabricator and then samples at each manufacturing stage: Bare coupon
Electronics Forum | Thu May 14 14:48:45 EDT 1998 | Dave F
We understand that testing for ionic contamination and surface insulation resistance measure different properties. We assemble printed circuit boards for other companies. We will not get combs on 90% of the boards that we assemble. We have no custo