Technical Library | 2023-01-17 17:22:28.0
The impact of voiding on the solder joint integrity of ball grid arrays (BGAs)/chip scale packages (CSPs) can be a topic of lengthy and energetic discussion. Detailed industry investigations have shown that voids have little effect on solder joint integrity unless they fall into specific location/geometry configurations. These investigations have focused on thermal cycle testing at 0°C-100°C, which is typically used to evaluate commercial electronic products. This paper documents an investigation to determine the impact of voids in BGA and CSP components using thermal cycle testing (-55°C to +125°C) in accordance with the IPC- 9701 specification for tin/lead solder alloys. This temperature range is more typical of military and other high performance product use environments. A proposed BGA void requirement revision for the IPC-JSTD-001 specification will be extracted from the results analysis.
Technical Library | 2023-01-17 17:19:44.0
A test program was developed to evaluate the effectiveness of vacuum reflow processing on solder joint voiding and subsequent thermal cycling performance. Area array package test vehicles were assembled using conventional reflow processing and a solder paste that generated substantial void content in the solder joints. Half of the population of test vehicles then were re-processed (reflowed) using vacuum reflow. Transmission x-ray inspection showed a significant reduction in solder voiding after vacuum processing. The solder attachment reliability of the conventional and vacuum reflowed test vehicles was characterized and compared using two different accelerated thermal cycling profiles. The thermal cycling results are discussed in terms of the general impact of voiding on solder thermal fatigue reliability, results from the open literature, and the evolving industry standards for solder voiding. Recommendations are made for further work based on other void reduction methods and additional reliability studies.
Technical Library | 2007-08-28 20:18:06.0
A conformal coating is defined as a thin polymeric material which covers the surface of an electronic assembly. These coatings are used to provide an electrically insulative and environmentally protective seal or cover to a completed printed circuit board (PCB).
Technical Library | 2016-11-09 19:22:54.0
Nordson MARCH found a solution for a manufacturer of PCBAs used in ruggedized environments. Read how plasma prior to conformal coating reduced defects and virtually eliminated coating-related failures.
Technical Library | 2015-01-05 17:38:26.0
The impact of voiding on the solder joint integrity of ball grid arrays (BGAs)/chip scale packages (CSPs) can be a topic of lengthy and energetic discussion. Detailed industry investigations have shown that voids have little effect on solder joint integrity unless they fall into specific location/geometry configurations. These investigations have focused on thermal cycle testing at 0°C-100°C, which is typically used to evaluate commercial electronic products. This paper documents an investigation to determine the impact of voids in BGA and CSP components using thermal cycle testing (-55°C to +125°C) in accordance with the IPC-9701 specification for tin/lead solder alloys. This temperature range is more typical of military and other high performance product use environments. A proposed BGA void requirement revision for the IPC-JSTD-001 specification will be extracted from the results analysis.
Technical Library | 2011-11-16 22:11:58.0
Flexible Circuits are proven, reliable interconnect solutions for many of today's electronic packages. This article gives some general guidelines in terms of "dos" and "don'ts" that will help the engineer or designer make better decisions when using flex
Technical Library | 2012-08-02 21:05:14.0
First published in the 2012 IPC APEX EXPO technical conference proceedings. Pure tin is a common finish for copper hook up wire, coaxial cable, ground braid and harness assemblies used on electronic assemblies. Historically there have been fewer reports o
Technical Library | 2007-06-13 13:44:10.0
Very high performance computer applications have created a demand for large organic substrates capable of interconnecting one or a few ASIC semiconductor devices with packaged memory devices. The electrical advantages offered by the use of a thin PTFE composite substrate were coupled with intrinsic mechanical advantages to create very high performance applications. The application development required interactions of design, fabrication, and new manufacturing technology to obtain rapid prototype production and allow a successful ensuing manufacturing ramp.
Technical Library | 2021-04-15 14:39:41.0
Inspection of printed circuit board (PCB) has been a crucial process in the electronic manufacturing industry to guarantee product quality & reliability, cut manufacturing cost and to increase production. The PCB inspection involves detection of defects in the PCB and classification of those defects in order to identify the roots of defects. In this paper, all 14 types of defects are detected and are classified in all possible classes ...
Technical Library | 2017-06-01 17:12:08.0
The corrosion of Nickel-Palladium-Gold (Ni-Pd-Au) finish terminals in humid environments is known to be reduced with the application of a conformal coating such as acrylic. Corrosion has a higher rate of occurrence around the terminal ‘knee’ of a surface mount component, which may be reduced with the application of conformal coatings. Although radio frequency (RF) plasma processing is generally known to enhance conformity of conformal coating to surfaces through ionic bombardment, the effect on the functionality of assembled printed circuit boards (PCB) is not as well known. The purpose of this study is to assess whether RF plasma processing can enhance the adhesive and coverage qualities of an acrylic conformal coating on PCBs, specifically on Ni-Pd-Au terminals with a knee, and if plasma processing has an effect on the electrical functionality of components and fully assembled PCB.