Electronics Forum | Thu May 30 08:04:25 EDT 2002 | zanolli
Hello Russ, I'm not quite sure I understand your question. Are you saying that you must hand solder these connectors because the gold plating doesn't allow other though hole processing methods to wet the solder the length of the pin in the PTH? Reg
Electronics Forum | Wed May 29 19:17:17 EDT 2002 | russ
We are starting to see a large increase in the use of through board gold plated connectors that require hand soldering with the limitation of .o6" encroachment up the pin. What is the best way to accomplish this? we currently scrap about 5-10% of t
Electronics Forum | Fri May 31 17:04:02 EDT 2002 | davef
We use boots / shunts er wutt ever you call them to protect solderable component surfaces from wave soldering. Not sure how it would work in your case try: * Kinnarney Rubber 450 Main St. P.O.Box 37 Mantua, N.J. 08051 609-468-1320 fax 7438 http://ww
Electronics Forum | Fri May 31 08:51:09 EDT 2002 | zanolli
Hello Dave, As related to connector mating interface, fretting corrosion is the oxidation of the contact points, causing high resistance across the interface. Fretting corrosion is caused my micromotions in the interface exposing the metalized conta
Electronics Forum | Fri Feb 28 01:08:33 EST 2020 | sarason
Back in the 50's, 60's and 70's gold plated boards were all the rage for high reliability. test equipment, milspec etc. Nowadays only edge connectors are gold plated. Immersion plated gold is also used but it doesn't last the distance like gold plate
Electronics Forum | Fri Jun 14 14:30:36 EDT 2002 | davef
Assuming you are talking about solderable surfaces: People specify various materials to protect the solderability of the pads on the board. Gold, actually, Electroless Nickel - Immersion Gold [ENIG], is popular. * Board fabricators like it because
Electronics Forum | Fri Jul 02 09:54:02 EDT 1999 | John Thorup
| | | | We are wave soldering some fabs with a lot of unmasked trace area along the edges. The trace area is solid copper covered with tin / lead, no masking, no components along the edges, same on solder side and component side (goofy board design)
Electronics Forum | Fri Jul 02 10:06:17 EDT 1999 | John Thorup
| | | | We are wave soldering some fabs with a lot of unmasked trace area along the edges. The trace area is solid copper covered with tin / lead, no masking, no components along the edges, same on solder side and component side (goofy board design)
Electronics Forum | Mon Nov 27 22:01:25 EST 2017 | bibi11952
Hello SMTNet, We had received boards from our CM, some came with a Tin plated finish on the SMT hermaphroditic edge connector, while others came with Gold plated on the same connector. Tyco supplies both version and they apparently mixed up parts.
Electronics Forum | Tue Dec 10 05:03:58 EST 2002 | praveen
We are having solder fillet finish issue. The solder looks like rough solder on the connector leads .The plating of the leads is Nickel (99.9% purity) and the PCB plating is imersion gold. I have tried fine tuning my reflow profiles an have used N2 i