Electronics Forum | Wed Feb 27 13:11:04 EST 2008 | tonyamenson
I was asked to post my finding about HumiSeal stripper for polyurethane coating. Both as an information sharing as well as someone who may offer advice on teh situational use of 1063 solvent stripper. So here is what I found: The stripper worked t
Electronics Forum | Thu Sep 04 21:50:47 EDT 2003 | davef
We like to use "enameled wire" that can be stripped by hot solder. Formvar [105�C] will not do that. Formvar was designed to with stand the hot oil seen in transformers. So, it requires either chemical or mechanical stripping. Most polyurethanes
Electronics Forum | Sat Mar 28 06:59:03 EDT 2015 | robertwillis
I would agree with the comments so far its much better to have some pre heat. You have not explained why bottom side preheat is a problem. Even having some input will help balance the process. Assume there is some thing on the back side that is a pro
Electronics Forum | Sat Jul 17 03:02:58 EDT 1999 | Jeff Sanchez
| | | | | I need a good chemical to remove the lacquer finish off of magnet wire. I know there are different kinds but I need one that really works. Any suggestions would be great. thanks in advance guys. | | | | | | | | | What is it you're trying t
Electronics Forum | Sat Jul 17 01:23:29 EDT 1999 | Scott McKee
| | | | I need a good chemical to remove the lacquer finish off of magnet wire. I know there are different kinds but I need one that really works. Any suggestions would be great. thanks in advance guys. | | | | | | | What is it you're trying to do?
Electronics Forum | Sat Jul 17 13:25:02 EDT 1999 | Scott
| | | | | | I need a good chemical to remove the lacquer finish off of magnet wire. I know there are different kinds but I need one that really works. Any suggestions would be great. thanks in advance guys. | | | | | | | | | | | What is it you're tr
Electronics Forum | Fri Oct 16 21:17:04 EDT 1998 | Scott McKee
| | With current soldering of stranded wires to pcb assy's the wire tends to be very brittle and can break with very little movement of the wire. We use a low residue cored wire. Anybody with advice or who has seen a similar problem/knows how to over