Electronics Forum | Wed Apr 11 22:05:58 EDT 2001 | davef
OA pastes are more hydroscopic than NC pastes. Hydroscopic. The capacity of a material to absorb and retain moisture from the ambient air. Sometimes this is compounded if you remove paste from the frig and let it warm to room temperature, because
Electronics Forum | Tue Aug 28 11:12:23 EDT 2007 | grics
This is what I was thinking, but I am being beat up pretty badly by the selective solder. Ambient temperature is anywhere in the the neighborhood of 76 - 80 degrees F. I am not sure of the RH, but I wouldn't think that would be my issue... One of
Electronics Forum | Wed Jan 03 21:20:22 EST 2007 | davef
Comments are: * General purpose RTV (RTV-108) releases an acetic acid (vinegar) during cure and corrodes copper, brass and sensitive metals. It is therefore NOT for use in delicate electrical or electronic applications. However, there is an electrica
Electronics Forum | Wed Mar 05 12:23:31 EST 2003 | msivigny
Hello Phil, We did use an Oracle relational database with an Access front end to input and query data from the system for reports. We did not perform SPC with the Oracle dB. As the whole data collection process was completely customized, we hadn't im
Electronics Forum | Thu Apr 21 11:43:03 EDT 2005 | davef
We understand the problem of trying to coat over RTV. We have seen the same problem with acrylic and urethane coatings not wanting to stick to RTV. Some acrylics seem to be worse than urethane. Since this is a new product, may be you could pot your
Electronics Forum | Tue Jul 17 21:48:09 EDT 2007 | davef
Per ESD Handbook TR 20.20 paragraph 5.3.15 Humidity "Humidity is beneficial in all ESD Control Program Plans. Contact and separation of dry materials generates greater electrostatic charges than moist materials because moisture provides conductivity
Electronics Forum | Mon Jul 16 15:44:27 EDT 2007 | davef
J-STD-001 doesn't necessarily require additional controls under conditions of low humidity, only that you verify the effectiveness of what you have in place. ESD S20.20 [1999] only says that relative humidity above 30% is "desirable". ESD S20.20 [200
Electronics Forum | Tue Dec 05 15:10:55 EST 2000 | Francois Monette
Victor, here are a few more elements of information to answer your question. Both the temperature and relative humidity on the manufacturing floor have a significant impact relative to the rate of diffusion of moisture inside a plastic package and t
Electronics Forum | Thu Aug 21 16:00:31 EDT 2014 | davef
This links to a NPL presentation on moisture removal from PCB http://www.npl.co.uk/upload/pdf/20140318_effect_baking.pdf Consider: * Focusing on preventing moisture contamination of boards, rather than removing moisture * There will be no standard
Electronics Forum | Sun Sep 07 20:51:52 EDT 2014 | natashakt
1. Is the high RH environment consistently at 72% RH and 21.4 degrees Celsius? No, over the past 2 weeks I have recorded the highest at the moment: 67% RH at 22.6 degrees C and lowest (it is Spring not summer yet): 31.9% RH at 19.0 degrees C. Or d