Technical Library | 2023-01-17 17:19:44.0
A test program was developed to evaluate the effectiveness of vacuum reflow processing on solder joint voiding and subsequent thermal cycling performance. Area array package test vehicles were assembled using conventional reflow processing and a solder paste that generated substantial void content in the solder joints. Half of the population of test vehicles then were re-processed (reflowed) using vacuum reflow. Transmission x-ray inspection showed a significant reduction in solder voiding after vacuum processing. The solder attachment reliability of the conventional and vacuum reflowed test vehicles was characterized and compared using two different accelerated thermal cycling profiles. The thermal cycling results are discussed in terms of the general impact of voiding on solder thermal fatigue reliability, results from the open literature, and the evolving industry standards for solder voiding. Recommendations are made for further work based on other void reduction methods and additional reliability studies.
Technical Library | 2023-09-07 14:38:31.0
A repeat customer specializing in high-technology interconnect, sensor, and antenna solutions, partnered with us to dispense small volumes of solder paste (Indium 10.1 SAC305 T6SG 78%m) onto backplane connectors – gold pads 0.175mm x 0.225mm. We performed a test requiring 0.200mm diameter or smaller dots to demonstrate the dispensing capability required.
Technical Library | 2020-12-02 20:36:54.0
Industry 4.0 is a topic of much discussion within the electronics manufacturing industry. Manufacturers and vendors are trying to come to terms with what that means. In the most simplistic of terms, Industry 4.0 is a trend toward automation and data exchange within the manufacturing process. This basically requires connectivity and communication from machine to machine within the manufacturing line. The challenge is to collect data from each of the systems within the line and make that data available to the rest of the machines. Without test and inspection, there is no Industry 4.0. The whole purpose of test and inspection is to collect actionable data that may be used to reduce defects and maximize efficiency within the manufacturing line. The goal is to minimize scrap and get a really good handle on those process parameters that need to be put in place to manufacture products the right way the first time. For maximum efficiency, three inspection systems are required within the production line. These are solder paste inspection (SPI) post-solder deposition, automated optical inspection (AOI) post-placement, and AOI post-reflow. This requires a substantial investment; however, the combination of all three inspection machines is really the only true way to provide feedback for each stage of the manufacturing process.
Technical Library | 2023-12-15 03:06:24.0
The first process in the SMT industry is solder paste printing. After the solder paste printing is completed, electronic components are attached to PCB pads through a SMT machine, and then reflow soldered. A preliminary PCB board is roughly processed. SMT is a combination of multiple devices, and such a line is called an SMT production line. Our common PCBA is processed through this process. In SMT technology, each process is very important, and poor quality can be caused by different process defects. Today, we are discussing the causes and countermeasures of SMT printing collapse.
Technical Library | 2019-05-24 09:22:59.0
There is a smaller process window and a much narrower margin of error when creating and using lead-free reflow profiles for surface mount parts on printed circuit boards (PCBs). Solder balls, dewetting, tombstones, voids, and head-on-pillow problems will occur much more frequently because lead-free alloys behave differently than eutectic pastes. Problems are compounded due to the extra heat necessary for some lead-free pastes to reach their melting points.
Technical Library | 2020-05-08 18:22:31.0
A customer contacted the Helpline to perform analysis on a lead-free assembly which exhibited intermittent functionality. The lead-free assembly exhibiting intermittent functionality when pressure was applied to the ball grid array (BGA) packages. Industrial adaptation of a Restriction of Hazardous Substances (RoHS) compliant solder standard has created a new host of failure modes observed in lead-free assemblies. Pad cratering occurs when fractures propagate along the epoxy resin layer on the underside of the BGA connecting pads. While originating from process, design, and end use conditions, it is the combination of a rigid lead-free solder with inflexible printed circuit board (PCB) laminates that has advanced the prevalence of this condition. Pad cratering is simply the result of mechanical stress exceeding material limitations.
Technical Library | 2019-06-20 07:45:19.0
One of the two basic risks of employing the commercially accepted, Restriction of Hazardous Substances (RoHS) compliant, lead-free (Pb-free) electronics is the threat to the electronics reliability from the growth of tin whiskers. The other basic risk deals with Pb-free solder joint reliability.
Technical Library | 2019-06-11 09:36:13.0
An experiment was recently performed ACI Technologies for a customer that was interested in comparing the wetting of lead-free solders with varying temperature profiles and atmospheric conditions. In order to deliver an objective measurement of solder wetting (in addition to subjective inspection analysis), a simple wetting indicator pattern was added to the solder stencil in an area on the test vehicle that had exposed and unused copper.
Technical Library | 2020-07-01 19:45:04.0
A company approached ACI Technologies (ACI) for assistance with a new product that was about to undergo its initial proof-of-concept prototype build. This product was an item that was being furnished to the Department of Defense for a program designed to increase the technical capabilities of computer equipment issued to the war fighter. The requirements for this item specified the use of tin-lead solder during assembly of production units. One of the main responsibilities for ACI during this project was to assist the client in mitigating the risk introduced using commercial off-the-shelf materials that may be lead-free.
Technical Library | 2023-09-18 03:40:02.0
Our SMT intelligent solder paste supply system is the perfect solution for businesses that need to improve the accuracy and consistency of their SMT paste printing. Our system uses the latest technology to automatically dispense the correct amount of solder paste to each stencil opening, ensuring that your SMT assemblies are consistently high-quality.