Electronics Forum | Tue May 14 22:09:04 EDT 2013 | ultimatejoker
Hi, what is significant different between PdNi and PdCo Plating? I found in some papers indicate that the deposit characteristics for both plating is totally the same.
Electronics Forum | Mon Jul 18 12:24:53 EDT 2016 | oleksz
Some people involved in PCB assembly process claim that SMD components reflow soldering problems are often caused by traces running under a component. According to this claim, trace (or any copper) covered by solder mask and placed under SMD componen
Electronics Forum | Mon Jul 18 12:25:30 EDT 2016 | oleksz
Some people involved in PCB assembly process claim that SMD components reflow soldering problems are often caused by traces running under a component. According to this claim, trace (or any copper) covered by solder mask and placed under SMD componen
Electronics Forum | Fri Jun 19 13:40:25 EDT 1998 | Terry Burnette
| Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | Mike There has been a
Electronics Forum | Fri Jun 19 14:25:24 EDT 1998 | Earl Moon
| | Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | | Mike | There has b
Electronics Forum | Fri Jan 15 07:23:14 EST 2021 | denism
Also, solder splashes can be due to contamination, for example, on the terminals of components. In the past, had a problem with solder splashes on a seemingly standard SMD component. The reason was the incorrect nickel plating process of the componen
Electronics Forum | Thu Jun 25 09:53:04 EDT 1998 | Earl Moon
| | Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | | Mike | Mike, | You
Electronics Forum | Wed Jun 24 16:23:29 EDT 1998 | Justin Medernach
| Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | Mike Mike, Your concer
Electronics Forum | Fri Jun 19 10:03:46 EDT 1998 | Earl Moon
| Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | Mike Mike, We and ind
Electronics Forum | Tue Oct 07 12:35:10 EDT 2008 | andy_pal
Hi All, I am using COB on my DOUBLE SIDED PCB. lastly we used Eletrolytic Ni / Flash Gold Plating. Our Boards vias Failed the UL corrosion Test. we did some cross-section analysis and found 10.75 �m of Nickel and 0.022 um of Gold and as the Process