Electronics Forum | Tue May 12 10:03:12 EDT 2009 | daan_terstegge
Hi All, I see more and more components like QFN or LGA with bottom-only terminations,with landpatterns getting finer all the time. I have no ppm-figures of our process, but based on a benchmark study by Agilent I'd say that 500 ppm is a decent value
Electronics Forum | Wed May 20 17:56:51 EDT 2009 | dyoungquist
I have attached a pdf showing the dimensions for the QFN we placed. First, The pins on the part are not only on the bottom side but also wrap around to come up each of the 4 sides of the part as shown in the side view in the attached pdf. This i
Electronics Forum | Tue Sep 18 11:34:36 EDT 2001 | jschake
The tightest spacing between neighboring 0201 components assembled was 8-mils. Please refer to the response for the query entitled �Minimizing Tombstoning Defects� posted by martys, as the response provided there is also relevant to address this que
Electronics Forum | Tue Nov 28 21:16:17 EST 2006 | davef
J Rose at EMPF says: The introduction of no-clean solder fluxes in electronics manufacturing has given rise to greater levels of solder balling simply because the opportunity to remove them in the wash process does not exist. They are typically cause
Electronics Forum | Fri Jan 15 07:23:14 EST 2021 | denism
Also, solder splashes can be due to contamination, for example, on the terminals of components. In the past, had a problem with solder splashes on a seemingly standard SMD component. The reason was the incorrect nickel plating process of the componen
Electronics Forum | Thu Jun 27 21:28:42 EDT 2002 | davef
You're correct that the Ni/Pd termination seems to have something to do with you solder balling. It could be related to the interaction between your paste and the Pd. I assume these are really 'fines' rather than 'balls'. Things that come to mind a
Electronics Forum | Wed Jul 19 12:54:04 EDT 2023 | calebcsmt
Since side fillets are not a requirement for QFNs/BTCs due to some packages not having wettable side terminations, how does one determine if the side terminations are actually solderable/designed for wetting? Is it simply if the side terminations
Electronics Forum | Fri Jun 29 14:15:00 EDT 2001 | stefo
This is a question about complying with J-STD-001 solderability testing. Do any of you have your vendors certify that the components and PCB's that you buy from them comply with the solderabilty requirements spelled out in the -002 and -003, in lieu
Electronics Forum | Thu May 13 20:40:25 EDT 2021 | winston_one
Yes, we can't use pure Pb PROCESS. And as I say we will not use it anyway, as we have lead-free BGA's, LGAs, component with Solder Charged Terminations... It's became almost normal practice to solder it with leaded solder pastes. In this case peak re
Electronics Forum | Tue Jan 23 11:55:27 EST 2001 | aiscorp
I gather from your question that you might have experienced large scale system implementation problems in the past, or at least fear experiencing it in the future. This is a very valid concern based on the performance of traditional CIM systems. Fo