Technical Library | 2021-03-04 15:16:27.0
Out-of-plane wrinkling has a significant influence on the mechanical performance of composite laminates. Numerical simulations were conducted to investigate the progressive failure behavior of fiber-reinforced composite laminates with out-of-plane wrinkle defects subjected to axial compression. To describe the material degradation, a three-dimensional elastoplastic damage model with four damage modes (i.e., fiber tensile failure, matrix failure, fiber kinking/splitting, and delamination) was developed based on the LaRC05 criterion. To improve the computational efficiency in searching for the fracture angle in the matrix failure analysis, a high-efficiency and robust modified algorithm that combines the golden section search method with an inverse interpolation based on an existing study is proposed.
Technical Library | 2021-10-12 18:01:49.0
The existence of counterfeit products, e.g., integrated circuits (ICs) and printed circuit boards (PCBs), in the modern semiconductor supply chain has seriously jeopardized the security and reliability of electronic systems, and has also caused the loss of suppliers' profit and reputation. Most of existing research papers prevent or detect counterfeit IC and PCB substrate separately, without testing the PCB as a whole, and often require the assistance of external equipment. In this article, a novel ring oscillator- based PCB authentication (ROPA) methodology to detect counterfeit PCB through supply chain is proposed, which ...
Technical Library | 2014-07-10 17:37:18.0
This paper studies and compares the effects of pull–pull and 3-point bending cyclic loadings on the mechanical fatigue damage behaviors of a solder joint in a surface-mount electronic package.The comparisons are based on experimental investigations using scanning electron microscopy (SEM) in-situ technology and nonlinear finite element modeling, respectively. The compared results indicate that there are different threshold levels of plastic strain for the initial damage of solder joints under two cyclic applied loads; meanwhile, fatigue crack initiation occurs at different locations, and the accumulation of equivalent plastic strain determines the trend and direction of fatigue crack propagation. In addition, simulation results of the fatigue damage process of solder joints considering a constitutive model of damage initiation criteria for ductile materials and damage evolution based on accumulating inelastic hysteresis energy are identical to the experimental results. The actual fatigue life of the solder joint is almost the same and demonstrates that the FE modeling used in this study can provide an accurate prediction of solder joint fatigue failure.
| 1 |