Another resource for BGA Rework is VJ Electronix, they manufacture SRT Rework systems.
Electronics Forum | Mon Jun 08 16:07:55 EDT 1998 | Igmar Grewar
Our company wants to buy a rework station for BGA's. I would like to know what is a good BGA rework station. IR or hot air? Do we need a rework station with optical placement or can BGa's be placed manually during rework. We have seen a demo of an ER
Electronics Forum | Tue Jun 09 10:09:22 EDT 1998 | Debbie Nizri
| Our company wants to buy a rework station for BGA's. I would like to know what is a good BGA rework station. IR or hot air? Do we need a rework station with optical placement or can BGa's be placed manually during rework. We have seen a demo of an
Electronics Forum | Fri Jun 12 13:47:20 EDT 1998 | Enza Hill
The SMTA Great Lakes Chapter (Chicago area) is holding a Rework Symposium on June 30th. (I know REWORK is a dirty job, but some of us have to do it!) We will have several speakers in the morning on the following topics: - Rework Management & Optimi
Electronics Forum | Thu May 06 05:29:46 EDT 1999 | Edmund Loh
Can anyone pls enlighten me on the rework of BGA. I reworking on a optic BGA with a glass plate on it. Is there any special requirement to take care for the rework. Thank You
Electronics Forum | Fri Mar 26 19:32:05 EST 1999 | Martin Dunning
I am a student doing a project on rework os BGAS and CSPS and Im looking for information on it especially rework of csps Has anyone got x-ray images of csps after rework or of BGAS to show csps with solder balls Appreciate any help Urgent!!!!
Electronics Forum | Tue Jan 08 17:47:15 EST 2002 | mantis
Well assuming that the parts are genuinely damaged when rejected and you want to rework them to reduce scrap,you could use a shadow graph and get the mechanical spec on clear film.Then rework accordingly you should be able to rework most leads.
Electronics Forum | Tue Jul 26 08:57:23 EDT 2011 | indyc
I am trying to rework FP4531 underfill. Some of the underfill flowed to adjacent capacitor and resistor. Even though the datasheet says that it is non-reworkable, has anyone tried reworking / removing excess underfill? Any information would be help
Electronics Forum | Mon Mar 29 14:29:50 EST 2004 | davef
Few people underfill PBGA. People underfill CCGA, uBGA, and FC. Consider a reworkable underfill on those devices that you expect to rework. Reworkable underfill candidates * Thermoset: ME526 (Red) * Loctite: 3567 (Cream) * Dexter: FP 4511 (Black)
Electronics Forum | Mon Jan 16 10:59:25 EST 2006 | davef
Ken Tacky flux reworked BGA will be perfectly reliable in most customer use environments. We do not have data, but the tacky flux reworked BGA will be less reliable than a BGA reworked with paste [assuming all other factors are the same], because t
.gif)