Electronics Forum | Wed Dec 19 09:24:21 EST 2012 | swag
Many times we manually add flux from the top side for good fill.
Electronics Forum | Mon May 14 16:36:58 EDT 2012 | davef
You're thinking correctly in trying to improve your process. Can you change to a more active flux? Look at the copper that connects to the center pin. You may need to relay-out the board to add a wagon wheel style thermal relief in that area.
Electronics Forum | Mon May 14 12:44:08 EDT 2012 | tomgervascio
I am a user of an Ersa Versaflow 3/45. I was wondering if anyone could share some process pointers. I have a 0.125" multilayer PCB that I am having problems consistently achieving 75 percent hole fill on a mini-coax connector. The coax connector ha
Electronics Forum | Fri Feb 08 10:52:24 EST 2019 | roblackey
BLT 31-41 "No Clean Selective Flux For Aerospace" On a Versaflow 3/45 Atomises well, good hole penetration, good wetting, cleans off well in the solvent cleaner. Use for SN100C, SA0307, and 60/40.
Electronics Forum | Fri Mar 22 14:07:00 EDT 2019 | proceng1
I believe that NORDSON now recommends AIM NC277. Nordson bought out ACE-protech.
Electronics Forum | Thu Feb 07 12:50:21 EST 2019 | gregcr
Hi All, What are you running for selective solder flux? I'd like any opinion on water soluble and/or no-clean fluxes you are using. In our Kiss 104 machine we use HYDRO-X20 water soluble flux, per the original install suggestion, but I'd like to k
Electronics Forum | Fri Mar 22 14:19:38 EDT 2019 | gregcr
Thank you ProcEng1 Nordson sent me a flux suggestion list: No Clean: 1. Kester Select 10 2. ALPHA EF-2210 3. AIM FX-16 Water Sol: KESTER 2331-ZX Nozzle Tinning: SUPERIOR #75
Electronics Forum | Wed Feb 13 13:30:03 EST 2019 | emeto
I personally prefer a NC process if I have to chose. AIM flux was good NC377 I think(they keep changing names), NF 372 from and many more. You can make them all work...the KISS 104 ...
Electronics Forum | Thu Aug 20 14:52:40 EDT 2009 | davef
Armando: We're guessing that the white residue is on the laminate also. We believe that the residue has something to do with your low residue flux and water. It could be: * Water contamination in the flux. * Poor selection of preheat temperature that
Electronics Forum | Sat Oct 01 11:48:45 EDT 2005 | Hiram
Hello everybody, We are in the process of implementing NC process on the wave solder. We have a Sonotek XL fluxing system. Any ideas out there? Solder used: SN100C Flux options so far: 264-5 flux, 270WR VOC-free 9both from AIM solder) The flux ch