Electronics Forum | Wed Jun 07 10:56:38 EDT 2006 | Chunks
In the past, I would normally tell out highly talented inspectors to leave the balls there. The were trapped in the flux residue and were hard to remove. Never caused a problem. But then there was an incident where someone had the bright idea to u
Electronics Forum | Thu May 13 18:36:55 EDT 1999 | Andrew Wulff
| | On 1.27mm (0.050 inches) Standard Ball Grid Array's. | | The ball size diameter starts at approximately 0.025 inches. | | | | If the ball size decreases to 0.012 inches (due to the solder flowing down a via) is the solder connection reliable? |
Electronics Forum | Fri May 07 17:02:01 EDT 1999 | Earl Moon
| On 1.27mm (0.050 inches) Standard Ball Grid Array's. | The ball size diameter starts at approximately 0.025 inches. | | If the ball size decreases to 0.012 inches (due to the solder flowing down a via) is the solder connection reliable? | | This
Electronics Forum | Wed May 12 20:32:14 EDT 1999 | Earl Moon
| Earl | | you posted a message on 1-14-99 about converting to VOC free flux. Have you completed your evaluation? Could I get a copy of any data supporting your conversion to VOC free? | | Thanks | | WDR | | WDR, We are awaiting the latest dat
Electronics Forum | Tue Jun 04 17:21:22 EDT 2002 | jasonfang
I found solderballs are around chip components (on one side of middle area), I checked gerber data, solder paste of aperture on the stencil for these chip components have 5% reduction to solder land on PCB, shape of solder land are square, not home p
Electronics Forum | Thu Jan 02 10:31:48 EST 2020 | slthomas
It is strange that you're having issues while using the same process parameters (including stencil) that worked successfully before. It doesn't guarantee that it's not one of those parameters changing in a manner that's not apparent, but it does sugg
Electronics Forum | Fri Aug 24 13:21:59 EDT 2018 | babe7362000
What do others use as far as solder paste type, stencil thickness and aperature size for a .4mm Ball Pitch CSP. Ball diameter is .3mm. Please let me know your thoughts or what you use. Thanks
Electronics Forum | Thu Aug 30 13:06:10 EDT 2018 | emeto
I don't know your board, but for this specific part: 10mil round aperture on a 3.5mil stencil with type 4 paste wold be ideal
Electronics Forum | Thu Aug 24 15:37:50 EDT 2006 | Chunks
Hi Any, This is from an earlies thread "Solder Ball After Reflow Process". Date: August 16, 2006 01:52 PM Author: Russ Subject: Solder Ball After Reflow Process Oven settings are meaningless here. What does the board see? It is the paste we a
Electronics Forum | Sat Jun 18 08:03:58 EDT 2005 | davef
kenscj: Responding to your points of interest: * On the smoothness of BGA solder balls causing solder ball misalign, void, solder short after reflow: We expect the solder balls to be smooth and have no sharp irregularities. We can't recall attribut