Electronics Forum | Wed Dec 28 16:03:53 EST 2005 | Chris
I have lots of experience with thermosonic gold ball bonding. You can read the literature and you will probably find some papers that say you can do it. I have never been able to do it. We gold ball bond all day long with little problems at all bu
Electronics Forum | Thu Jun 08 11:37:44 EDT 2017 | jkitt84
davef, thanks for feedback. I talked with a plater who said they put copper before silver when plating brass. Would a complete stack of: Brass part, then 0.0001-0.0002" of copper, then 0.0005" of silver, then Tarniban anti oxidation. Sound reasonabl
Electronics Forum | Mon Aug 27 15:06:29 EDT 2001 | davef
This otta push Wolfgang over the top ... Recommended reading G.G. Harman, Wire Bonding in Microelectronics : Materials, Processes, Reliability, and Yield, 2nd edition, McGraw-Hill Electronic Packaging and Interconnection Series, 1997. G.G. Harman, R
Electronics Forum | Wed Nov 06 20:18:30 EST 2002 | davef
cvrgrrrl Your first thermal cycle with imm silver should be the easiest to solder. That you see copper indicates you did no soldering, got no wetting, produced no intermetallics, etc. Tell us again which components did not solder? Wuzzis "plug" t
Electronics Forum | Tue Aug 21 05:05:52 EDT 2007 | vangogh
Hi All, I would like to get some inputs regarding this.... I have bare PCB which were stored with kapton tape attached on the Au plated pads. These were stored for close to a year. Upon removal of kapton tape, we noticed discolorations on the edges o
Electronics Forum | Wed Aug 15 16:04:23 EDT 2001 | davef
First, responding to your question � Several things on copper dissolution in solder are: * A 50um copper wire will dissolve in 60Sn / 40Pb solder at: - 200�C solder in 55 seconds; - 250�C solder in 20 seconds; - 300�C solder in 5 seconds; - 350�C so
Electronics Forum | Sat Nov 14 08:05:54 EST 1998 | Earl Moon
| | | | I believe that gold fingers on my circuit boards are being | | | | contaminated and need to clean them with some chemical | | | | solution. Any recommendations. | | | | | | | Chuck: What is the type and source of your contamination? Dave
Electronics Forum | Sun May 30 08:50:42 EDT 1999 | Dave F
| Yes l know this problem keeps cropping up on the forum but l've missed some of the follow-ups. | | Our problem is that the lifting only occurs on 3% of production so actually detecting an improvement is difficult. We're actually having to inspect
Electronics Forum | Fri Sep 17 03:55:45 EDT 1999 | Brian
| We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a reco
Electronics Forum | Fri Sep 17 06:01:12 EDT 1999 | Earl Moon
| | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a re
.gif)