Electronics Forum | Wed Jul 09 14:57:42 EDT 2008 | ck_the_flip
I think what Chunks meant is... TOOLING = THOSE POTS So basically, if some of your SMT or Through-Hole parts move around via a redesign or a respin, you will incur tooling costs (TOOLING is "THOSE LITTLE POTS FULL O' SOLDER.") When you're research
Electronics Forum | Mon Aug 09 20:47:21 EDT 2004 | KEN
I think OA flux left on the pot would quickly looses its activity and become part of the dross waste stream, and smoke stream for that matter. Also, if your wave is setup properly your selective pallets will scour (push) the top of the lambda wav
Electronics Forum | Fri Jul 22 03:07:45 EDT 2005 | Joseph
Dear all, As we know there is a high risk of reliability issue due to lead contamination during mixture of NLF component at LF wave soldering process. But we have the following feed back from one of our customer as follow: Concerning the risk of m
Electronics Forum | Mon Feb 06 07:10:45 EST 2017 | emeto
I was actually thinking about the wave soldering machine.
Electronics Forum | Tue Dec 13 06:56:27 EST 2005 | adanhn
Hi Steve, What I came up with for our Soltec Sigma 6621 is to make a stainless steel wave solder bath insert.The insert with all its components eg. impeller, Chipwave assy, pump shafts, main wave assy etc. I will send for plasma nitride coating.Afer
Electronics Forum | Tue Feb 08 07:11:24 EST 2005 | teilo
We manufacture all titanium component parts for wave solder machines. For additional information on our products please visit our websit at http://www.teiloengineering.com
Electronics Forum | Mon Feb 06 22:38:46 EST 2017 | david_chiu
No matter in selective soldering or wave soldering process, higher pot temperature and longer wetting time can increase IMC thickness and joint strength(reliability), but as Daivf said, you need to care if the DIP component and bare PCB was damaged b
Electronics Forum | Mon Dec 05 11:22:54 EST 2005 | slthomas
I searched the archives, found one thread with one response (my own, which went unnoticed since this forum doesn't bump threads when they get responses), so I'm hoping a resurrection of sorts will generate some input. Anyone using one of these syste
Electronics Forum | Mon Sep 25 15:32:21 EDT 2023 | joeljacobo
hello colleagues, Hoping that everyone is doing well, I am reaching out to you in the hope that your experience can help me. We have a wave solder with sac0307 alloy and the pot has turned a golden color, at first I thought it was common tin oxidat
Electronics Forum | Wed Jun 13 19:03:17 EDT 2007 | sueph
Need some advice. A relay in the Ol' Treiber went out to the wave solder pot, causing the temp of the pot to spike up to 800 degrees F. Since the machine wasn't in use that afternoon, it is possible that the pot was that hot for 4 hours before it wa