Electronics Forum | Mon Mar 07 15:35:35 EST 2005 | John M
It has been my experience that the standard Fr4 material (Tg 135c) will discolor when processed at the new higher temperatures required for the high tin alloys... We have been using the High Tg Fr4 (Tg 170c) for many years to ensure this does not hap
Electronics Forum | Thu Sep 03 08:39:53 EDT 2009 | markhoch
I'd be more concerned with the pcb itself then I would be with standard SMT components. Are you using a PCB with a high Tg? (170 degrees C or greater)
Electronics Forum | Thu Sep 09 19:32:12 EDT 2021 | kumarb
Forgot to ask earlier - what is the TG rating for your laminate? If not selected already, use a high TG rating like TG155 or TG170 laminates for the ROHS temps. Never saw swollen PCBAs with such rated PCBs to date.
Electronics Forum | Thu Sep 03 11:38:28 EDT 2009 | dyoungquist
I'd be more concerned with the pcb itself then I > would be with standard SMT components. Are you > using a PCB with a high Tg? (170 degrees C or > greater) The circuit board material is NP-170B (Nan Ya Plastics Corporation). It has a Tg of 170
Electronics Forum | Wed Feb 02 22:10:30 EST 2005 | T2
Higher Tg values are only one thing to look out for. Two other things that are very important to watch are the Td or Decomposition Temperature (the temperature that the epoxy actualy starts to break down), and the CTE for the material. Some Tg 14
Electronics Forum | Thu Feb 02 09:16:57 EST 2006 | lyrtech
Hi, I have some questions about material used in PCB for RoHS compliancy. It seems to be fuzzy between may manufacturer. Here are my questions: 1) What is the recommended material for lead-free assembly? 2) What's the difference between FR4 High Tg
Electronics Forum | Wed Jan 13 04:27:00 EST 2016 | crystalpcb
Hi Here is our factory production capability: Shenze Electronic PCB Specification Layer Count 1 to 35 Layers Material Brand Shengyi,KB,GRACE,ISOLA,Rogers,Taconic,ARLLON,Bergquist Base Material FR-4（TG135,TG150,TG170,TG180），Halogen Free FR-4，Ceramic
Electronics Forum | Fri Jun 09 11:55:34 EDT 2006 | jbrower
Howdy Amol, As far as I can see, there aren't too many pitfalls with SN100C. Just make sure to keep all of your alloys seperated. The issues that I am working out right now is the profiles with our wave pallets and some of our larger components. We