Electronics Forum | Fri Dec 01 14:12:50 EST 2000 | Jim M.
My company currently uses water soluble paste for our SMT process. We were having trouble retaining hot water in our in line, closed loop DI cleaner. The cleaner kept shutting down when the water temp. dropped below 125C. As a result, the conveyor
Electronics Forum | Fri Dec 01 16:02:33 EST 2000 | Jim M
Thanks for your reply. I 've tried to clarify and answer your questions. The water soluble paste used is WS3060, type 4. The boards are sent through a inline di cleaner after reflow. There is a hot Di waterwash, rinse and then hot air to dry the wa
Electronics Forum | Fri Dec 01 17:03:57 EST 2000 | Dave F
Curious, very curious ... Residues � Where are these residues? [solder & laminate / mask, solder only, laminate / mask only] What is the result of your analysis to the residues? How do you know it�s a flux residue, rather than a chemical by product
Electronics Forum | Fri Dec 01 15:37:50 EST 2000 | Dason C
Jim, you may need to look with different paste instead of the cleaning solvent. Please advise what is the paste which you currently using? Beside, when you talking about the board stayed in hot area, is it a drying area or the cleaning zone. If it
Electronics Forum | Fri Jul 23 14:41:41 EDT 2004 | Steve Stach
Dear JSK, It sounds like the root causes of your problem are two fold. First, excessive heat will polymerize the abietic acid found in rosin forming neo-abietic diamers and polymers which are much less soluble than the parent monomer. There are
Electronics Forum | Fri Mar 31 11:56:36 EDT 2017 | jutikagokarn
We are trying to build two different PCBs - one with no wash flux solder paste and the other with a washable flux solder paste. How difficult is it to use the same SMT line and switch between the two pastes? I assume there will be some cleaning invol
Electronics Forum | Fri Mar 31 15:58:07 EDT 2017 | jutikagokarn
Thank you for your response. We build boards on an SMT line that is shared with other companies too and are currently using water soluble flux based solder paste on both boards. We realized an issue with washing on one of the boards so requested to
Electronics Forum | Thu Jan 27 11:23:45 EST 2005 | russ
Well first off I wouldn't evaluate paste for a wave process. I would use solder bar instead. Flux - top side fillets and no shorting on the solder side, does it clean well after processing if using water soluble flux. How wide is the process win
Electronics Forum | Wed Oct 06 12:03:12 EDT 1999 | Graham Naisbitt
| | Hi, | | | | Help! Could anyone help to enlighten me on this? | | | | Question: | | | | If I have a CSP/BGA package of size X by Y and the standoff gap between the component and PCB is Z, What is the maximum allowable Y/Z or X/Z that using a n
Electronics Forum | Wed Oct 06 03:58:25 EDT 1999 | Brian
| | Hi, | | | | Help! Could anyone help to enlighten me on this? | | | | Question: | | | | If I have a CSP/BGA package of size X by Y and the standoff gap between the component and PCB is Z, What is the maximum allowable Y/Z or X/Z that using a n