Electronics Forum | Tue Jan 31 15:51:04 EST 2006 | russ
Relays huh? I can tell you from previous experience that relays are not a good heat gun candidate. Did you check how long this part can withstand the 240? I do not know what the 4 setting is on a liester but it is probably well in excess of the 24
Electronics Forum | Tue Jan 31 15:40:44 EST 2006 | mgdrouin1
Comp is relay. I've pulled the spec. Max 240. Using Leister h/g with manual temp settings from 1-6 (20 - 600C)set by the operator. Gun was set to setting 4. They are using the heat gun to reflow the solder after SMT but before wave. High fai
Electronics Forum | Wed Feb 01 08:12:04 EST 2006 | Chunks
OK, this is easy. You say HIGH fall out, so I can assume 25 or 50%? If so, run 10 without the heat gun and 10 with. This should show you if the heat gun process is the cause or not. If the relay is a surface mount, hand solder them on. If it's a
Electronics Forum | Mon Jul 03 05:39:05 EDT 2006 | ronalds
Hi, I am experience problems while testing wave soldering SMT components that are glued on the solderside (lead free). Between de leads of SOx type IC's and SOT's develop a great deal of solder beads. I have been using a RSS temp.profile while spr
Electronics Forum | Thu Jul 06 12:52:35 EDT 2006 | samir
..and he can put the flux in and keep it a secret too from his customer.. RSS profile on wave?? I never heard of a soak zone for wave preheat...you may be burning off your activator..hence, the beads. For wave preheat, your main goal is to ramp up
Electronics Forum | Mon Dec 17 12:06:58 EST 2007 | pjc
5 Steps to Eliminate Bridges: 1. Establish (wave) Parallelism First and foremost, you must establish board-to-wave parallelism. This is the prerequisite to any wave solder process control. For an understanding of the power of this approach go to ht
Electronics Forum | Mon Dec 17 11:55:08 EST 2007 | chef
I recently had the same problems, solder bridges on every thing I made, different customers boards, etc. I wave with no-clean flux. As I sorted out problems (pin holes, blow holes, splatter, etc.) I found a lot of variable factors. I changed flux,
Electronics Forum | Tue Feb 27 20:53:10 EST 2007 | davef
We'll guarantee the two pads are too close together. The proper spacing depends on the orientation of the parts to the wave. * Do the pads hit the wave at the same time? * Does one pad hit the wave before the other? If so, which? * How does the 06
Electronics Forum | Wed Feb 28 11:43:20 EST 2007 | realchunks
Marcin, Think outside the box. If you are glueing the SMT part down, why not have an aperture cut in your stencil (or recut a stencil) between the SMT part and thru-hole. Wave solder hates SMT glue. This will get rid of your solder short problem
Electronics Forum | Tue Feb 27 11:03:09 EST 2007 | Marcin
Hi All, Anybody knows what is the minimum clearance between through hole component and chip component? Problem description: On bottom side of my pcb are only 0603 chip components mounted on glue. One of the component is located very close to hole
.gif)