Technical Library | 2023-01-17 17:19:44.0
A test program was developed to evaluate the effectiveness of vacuum reflow processing on solder joint voiding and subsequent thermal cycling performance. Area array package test vehicles were assembled using conventional reflow processing and a solder paste that generated substantial void content in the solder joints. Half of the population of test vehicles then were re-processed (reflowed) using vacuum reflow. Transmission x-ray inspection showed a significant reduction in solder voiding after vacuum processing. The solder attachment reliability of the conventional and vacuum reflowed test vehicles was characterized and compared using two different accelerated thermal cycling profiles. The thermal cycling results are discussed in terms of the general impact of voiding on solder thermal fatigue reliability, results from the open literature, and the evolving industry standards for solder voiding. Recommendations are made for further work based on other void reduction methods and additional reliability studies.
Technical Library | 2023-01-17 17:12:33.0
Reflowed indium metal has for decades been the standard for solder thermal interface materials (solder TIMs or sTIMs) in most high-performance computing (HPC) TIM1 applications. The IEEE Heterogeneous Integration Thermal roadmap states that new thermal interface materials solutions must provide a path to the successful application of increased total-package die areas up to 100cm2. While GPU architectures are relatively isothermal during usage, CPU hotspots in complex heterogeneously-integrated modules will need to be able to handle heat flux hotspots up to 1000W/cm2 within the next two years. Indium and its alloys are used as reflowed solder thermal interface materials in both CPU and GPU "die to lid/heat spreader" (TIM1) applications. Their high bulk thermal conductivity and proven long-term reliability suit them well for extreme thermomechanical stresses. Voiding is the most important failure mode and has been studied by x-ray. The effects of surface pretreatment, pressure during reflow, solder flux type/fluxless processing, and preform design parameters, such as alloy type, are also examined. The paper includes data on both vacuum and pressure (autoclave) reflow of sTIMs, which is becoming necessary to meet upcoming requirements for ultralow voiding in some instances.
Technical Library | 2023-09-15 11:16:39.0
Elevate your electronics manufacturing with the SMT Offline X-Ray Machine. Achieve comprehensive component inspection and reliability assurance through advanced X-ray technology.
Technical Library | 2023-09-15 11:14:33.0
Optimize your inventory management with our SMD SMT X-Ray Offline Component Counting Machine. Ensure precise and efficient component counting with advanced X-ray technology. Enhance your operational efficiency and inventory accuracy for SMD and SMT components. Explore how this machine can revolutionize your component counting process and streamline your operations.
Technical Library | 2023-09-15 11:15:49.0
Experience unmatched component inspection precision with our SMT Offline X-Ray solution. Detect defects, ensure quality, and boost production efficiency with advanced X-ray technology.
Technical Library | 2023-09-15 11:17:10.0
Ensure the integrity of your components with our SMT Offline X-Ray System. Detect hidden defects and improve the quality of your PCBAs with precise X-ray inspection technology.
Technical Library | 2019-09-23 09:35:00.0
Failure analysis (FA), by its very nature, is needed only when things goawry. Before any testing is performed on the sample, a decision mustbe made as to whether or not the sample is allowed to be destroyedin the process of testing. Non-destructive testing can allow for re-use of the assembly since the functionality is not altered, but there still remains the possibility that inadvertent damage can occur through the course of the analysis. If non-destructive testing is preferred, then the following types of analysis can be performed. The testing can be divided into four categories: visual, X-ray (X-ray imaging and X-ray fluorescence), cleanliness (resistivity of solvent extract, ion chromatography, and Fourier transform infrared spectroscopy), and mechanical (non-destructive wire bond pull).
Technical Library | 2020-11-09 16:59:53.0
A customer contacted ACI Technologies regarding a high failure rate of their assemblies. They provided assemblies to be X-rayed and inspected for the purpose of identifying any process related issues such as (but not limited to) solder and assembly workmanship and evidence of damage due to moisture related problems during reflow (a.k.a. "popcorning"). Moisture damage usually appears as physical damage to the component. The first indication of moisture damage would be externally observable changes to the package in the form of bulging or fractures to the outer surface of the component, an example of which is shown in Figure 1. Internally observable indicators of moisture damage typically include fractures to the die inside the package and lifted or fractured wire bonds. These conditions would be apparent during transmissive X-ray inspection. Another symptom of moisture related damage would be inconsistent solder joint sizes that result from package deformation during the liquidus phase of the reflow process. None of these indicators of moisture related damage were present on the customer samples.
Technical Library | 2019-05-24 09:27:33.0
Decapsulation, or de-cap, is a failure analysis technique which involves the removal of material packaging from an integrated circuit (IC). After de-cap, visual inspection by optical microscopy of the internal circuitry may reveal areas where damage is most likely to have occurred. In addition, scanning electron microscopy (SEM) with energy dispersive x-ray spectroscopy (EDS) can identify the composition of any anomalies present after de-cap under higher magnification. The removal process of package material can be done either mechanically or chemically depending on the design of the integrated circuit. With ceramic packaging, de-cap is usually done mechanically by chiseling off the top with a fine razor and small hammer. For plastic packaging, de-cap requires chemical etching by strong acids. In this Tech Tips article, de-cap by chemical etching will be outlined step by step.
Technical Library | 2019-05-29 10:38:59.0
Decapsulation, or de-cap, is a failure analysis technique which involves the removal of material packaging from an integrated circuit (IC). After de-cap, visual inspection by optical microscopy of the internal circuitry may reveal areas where damage is most likely to have occurred. In addition, scanning electron microscopy (SEM) with energy dispersive x-ray spectroscopy (EDS) can identify the composition of any anomalies present after de-cap under higher magnification. The removal process of package material can be done either mechanically or chemically depending on the design of the integrated circuit. With ceramic packaging, de-cap is usually done mechanically by chiseling off the top with a fine razor and small hammer. For plastic packaging, de-cap requires chemical etching by strong acids. In this Tech Tips article, de-cap by chemical etching will be outlined step by step.