Electronics Forum | Fri Sep 10 15:32:30 EDT 1999 | Earl Moon
| We have a product, with various PWBs, with over 600 parts each one (We are a low Volume/high mix company with an average component placement per PCB between 250 to 300 parts). This PWBs have 7 to 10, 20 mils pitch parts. We are having problems with
Electronics Forum | Fri May 15 21:59:42 EDT 1998 | Earl Moon
| Hi, | There has been a lot of disputes in our company | about changing present HASL to another Finishing | which can provide more flatter pad surface in fine | pitch applications. ( perhaps Ni/Au, OSP ) | The target is to reduce solder defects, t
Electronics Forum | Fri Jul 30 14:50:26 EDT 1999 | Kevin Hussey
| I received a request from customer to assemble ceramic substrate (alumina oxide)that printed with a low temperature Copper thick film conductor (the overglaze layer is polymer). The Copper pads are exposed without any coating. | This ceramic substr
Electronics Forum | Mon May 18 20:57:06 EDT 1998 | Earl Moon
.025" pitch so the only problem we run into is too much HASL on the adhesive side causing improper glue dispense. | As Earl keeps saying HASL thickness is hard to impossible to control. I think we need to look hard at OSP's again but then you get in
Electronics Forum | Mon May 18 22:54:04 EDT 1998 | Dave F
.025" pitch so the only problem we run into is too much HASL on the adhesive side causing improper glue dispense. | | As Earl keeps saying HASL thickness is hard to impossible to control. I think we need to look hard at OSP's again but then you get
Electronics Forum | Mon Aug 28 17:04:52 EDT 2006 | Board House
ImSn - Immersion Tin - Not Recomended- short shelf life ImAg - Immersion Silver - Prefered Surface finsh by most Board houses, Best reworkablility, 12 moth self life, ENIG - Electroless Nickel Immersion Gold - Second Choice for Board Shops, 12 -
Electronics Forum | Wed Jul 04 12:35:19 EDT 2001 | davef
I thought I responded this this a while ago, guess NOT!!! Wow, Dano yagot Entek boards that are that old!!!! Coo. Sounds kwazy that you�d end-up with that volume of old boards, but it�s probably one of those deals where correcting the problem keep
Electronics Forum | Thu Jul 29 23:21:51 EDT 1999 | CH Lee
I received a request from customer to assemble ceramic substrate (alumina oxide)that printed with a low temperature Copper thick film conductor (the overglaze layer is polymer). The Copper pads are exposed without any coating. This ceramic substrate
Electronics Forum | Mon Apr 26 11:04:53 EDT 1999 | Dave F
| | Earl said, in essence: | | | | | Justin is absolutely right ... | | | | | | Again, Entek is not much more than a flux coating ... | | | | | | Metallic coatings protect best, as we all know - especially those electroplated. Those coatings chemi
Electronics Forum | Thu Jun 25 09:53:04 EDT 1998 | Earl Moon
| | Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | | Mike | Mike, | You